The effects of Ag on the microstructure and corrosion behavior of pre-soldering Sn-xAg lead-free solders,and on the formation of intermetallic layer of the solders with Cu substrate were investigated.The Ag contents(x...The effects of Ag on the microstructure and corrosion behavior of pre-soldering Sn-xAg lead-free solders,and on the formation of intermetallic layer of the solders with Cu substrate were investigated.The Ag contents(x)were 0,3.0,3.5,4.0,and5.0 wt.%.The Ag content played a role in the morphology of Ag3 Sn phase in the solders.The microstructure analysis showed that theβ-Sn phase was surrounded by eutectic networks in the 3.0 Ag and 3.5 Ag solders and large plate-like Ag3 Sn formed in the 4.0 Ag and5.0 Ag solders.Nonetheless,the Ag content slightly impacted the corrosion behavior of the as-cast solders as characterized using potentiodynamic polarization test.After soldering,only a single layer of a Cu6 Sn5 intermetallic compound formed at the Sn-xAg/Cu interface.By comparison,the Cu6 Sn5 intermetallic layer of the Ag-doped solders was thinner than that of the 0Ag solder.The fine Ag3 Sn particles in the eutectic networks precipitating in the 3.0 Ag and 3.5 Ag solders effectively hindered the growth of Cu6 Sn5 grains compared to large plate-like Ag3 Sn in the 4.0 and 5.0Ag solders.展开更多
The mechanical behavior of inherently anisotropic shale rocks under Brazilian test conditions are investigated in this study based on experimental studies and numerical simulations. The effects of the weak lamination ...The mechanical behavior of inherently anisotropic shale rocks under Brazilian test conditions are investigated in this study based on experimental studies and numerical simulations. The effects of the weak lamination planes and interlayer bonding force of these layers on the failure strength and fracture patterns are studied systematically. Numerical simulations using particle flow code in two dimensions based on the discrete element method showed a good agreement with the experimental results in the failure strength and fracture patterns. The shale revealed strong anisotropic behavior with the failure strength perpendicular to the lamination plane greater than failure strength parallel to lamination plane. The failure strength of the different interlayer bonding force against the layer orientations changed significantly. Four types of fracture patterns were observed: curved fracture, broken-linear fracture, layeractivated fracture, and central-linear fracture. The observed fracture patterns are either or a combination of tensile and/or shear fractures. Increase in interlayer bonding strength decreased the quantity of micro cracks and this directly led to reduction in the anisotropic behavior. Overall the layer orientation and interlayer bonding force of the shale thus play a very important role in the anisotropic behavior of the shale.展开更多
Tribological behavior and wear mechanisms of mechanically milled Al5083 alloy and Al5083−5wt.%B4C composite at room temperature and 200°C were discussed.Results revealed that due to the oxidative wear at room tem...Tribological behavior and wear mechanisms of mechanically milled Al5083 alloy and Al5083−5wt.%B4C composite at room temperature and 200°C were discussed.Results revealed that due to the oxidative wear at room temperature,a mechanically mixed layer(MML)was formed to protect the surface of the samples.Under 80 N of load at room temperature,the milled Al5083 and the Al5083−5wt.%B4C samples showed evidence of abrasion with limited volume loss.In this case,the wear rates were 5.8×10−7 and 4.4×10−7 mm3/(m·N),respectively.At 200°C and under 80 N of applied load,severe wear occurred in the milled Al5083 sample,and wear rate reached 10.8×10−7 mm3/(m·N)while the Al5083−5wt.%B4C sample showed mild wear with local 3-body abrasion and the wear rate reached 5.3×10−7 mm3/(m·N).Strengthening mechanisms such as dislocation pinning and the Hall−Petch theory,high hardness and the load transfer effect were crucial in determining the wear behavior of the Al5083−5wt.%B4C composite.On the other hand,the milled Al5083 sample represented a relatively high wear rate at 200°C,which seemed to be related to the local grain growth and a drop in its hardness.展开更多
A water-quenching technique has been adopted to evaluate thermal shock fracture and fatigue behaviors of porous Si3N4 ceramics in an air atmosphere. The high-porosity Si3N4 ceramics exhibit a higher strength retention...A water-quenching technique has been adopted to evaluate thermal shock fracture and fatigue behaviors of porous Si3N4 ceramics in an air atmosphere. The high-porosity Si3N4 ceramics exhibit a higher strength retention and a better resistance to thermal shock fatigue because of its role of the pores as crack arresters.A dense and coherent surface oxide layer leads to a significant benefit in residual strength during thermal fatigue, however, an increased fatigue number to 30 th cycle cannot cause a further influence although a thicker oxide layer presents, which is attributed to holes defect and disappearance of part intergranular phase.展开更多
Four-point bending tests were conducted up to failure on eleven reinforced concrete (RC) beams and strengthening beams to study the effectiveness of externally pouring ultra high toughness cementitious composites (UHT...Four-point bending tests were conducted up to failure on eleven reinforced concrete (RC) beams and strengthening beams to study the effectiveness of externally pouring ultra high toughness cementitious composites (UHTCC) on improving the flexural behavior of existing RC beams.The strengthening materials included UHTCC and high strength grade concrete.The parameters,such as thickness and length of strengthening layer and reinforcement in post-poured layer,were analyzed.The flexural behavior,failure mode and crack propagation of composite beams were investigated.The test results show that the strengthening layer improves the cracking and ultimate load by increasing the cross section area.Introducing UHTCC material into strengthening not only improves the bearing capacity of the original specimens,but also disperses larger cracks in upper concrete into multiple tightly-spaced fine cracks,thus prolonging the appearance of harm surface cracks and increasing the durability of existing structures.Compared with post-poured concrete,UHTCC is more suitable for working together with reinforcement.The load?deflection plots obtained from three-dimensional finite-element model (FEM) analyses are compared with those obtained from the experimental results,and show close correlation.展开更多
文摘The effects of Ag on the microstructure and corrosion behavior of pre-soldering Sn-xAg lead-free solders,and on the formation of intermetallic layer of the solders with Cu substrate were investigated.The Ag contents(x)were 0,3.0,3.5,4.0,and5.0 wt.%.The Ag content played a role in the morphology of Ag3 Sn phase in the solders.The microstructure analysis showed that theβ-Sn phase was surrounded by eutectic networks in the 3.0 Ag and 3.5 Ag solders and large plate-like Ag3 Sn formed in the 4.0 Ag and5.0 Ag solders.Nonetheless,the Ag content slightly impacted the corrosion behavior of the as-cast solders as characterized using potentiodynamic polarization test.After soldering,only a single layer of a Cu6 Sn5 intermetallic compound formed at the Sn-xAg/Cu interface.By comparison,the Cu6 Sn5 intermetallic layer of the Ag-doped solders was thinner than that of the 0Ag solder.The fine Ag3 Sn particles in the eutectic networks precipitating in the 3.0 Ag and 3.5 Ag solders effectively hindered the growth of Cu6 Sn5 grains compared to large plate-like Ag3 Sn in the 4.0 and 5.0Ag solders.
基金supported by the National Natural Science Foundation of China(Grants 41572310,41272351,and 41227901)the Strategic Priority Research Program of the Chinese Academy of Sciences(Grants XDB10030301 and XDB10030304)
文摘The mechanical behavior of inherently anisotropic shale rocks under Brazilian test conditions are investigated in this study based on experimental studies and numerical simulations. The effects of the weak lamination planes and interlayer bonding force of these layers on the failure strength and fracture patterns are studied systematically. Numerical simulations using particle flow code in two dimensions based on the discrete element method showed a good agreement with the experimental results in the failure strength and fracture patterns. The shale revealed strong anisotropic behavior with the failure strength perpendicular to the lamination plane greater than failure strength parallel to lamination plane. The failure strength of the different interlayer bonding force against the layer orientations changed significantly. Four types of fracture patterns were observed: curved fracture, broken-linear fracture, layeractivated fracture, and central-linear fracture. The observed fracture patterns are either or a combination of tensile and/or shear fractures. Increase in interlayer bonding strength decreased the quantity of micro cracks and this directly led to reduction in the anisotropic behavior. Overall the layer orientation and interlayer bonding force of the shale thus play a very important role in the anisotropic behavior of the shale.
基金Authors would like to appreciate the former chief of Faculty of Materials&Manufacturing Processes of the Malek-Ashtar University of Technology,Professor EHSANI and the chief of the Composite Department,Dr.POURHOSSEINI along with the Razi and Kimiazi SEM labs and mechanical properties and SEM labs of Iran University of Science and Technology.Furthermore,the authors would like to thank Professor REZAEI,Ms.HAMIDI,and Ms.DAYYANI,Mr.SA'ADAT,and Mr.ATAEI from Iran University of Science and Technology.Special thanks to Mrs.KESHAVARZ,Ms.HAMEDANIZADEH,Ms.SHABANI,Ms.SHOJAEI and Mr.GANDOMKAR for their help and support.
文摘Tribological behavior and wear mechanisms of mechanically milled Al5083 alloy and Al5083−5wt.%B4C composite at room temperature and 200°C were discussed.Results revealed that due to the oxidative wear at room temperature,a mechanically mixed layer(MML)was formed to protect the surface of the samples.Under 80 N of load at room temperature,the milled Al5083 and the Al5083−5wt.%B4C samples showed evidence of abrasion with limited volume loss.In this case,the wear rates were 5.8×10−7 and 4.4×10−7 mm3/(m·N),respectively.At 200°C and under 80 N of applied load,severe wear occurred in the milled Al5083 sample,and wear rate reached 10.8×10−7 mm3/(m·N)while the Al5083−5wt.%B4C sample showed mild wear with local 3-body abrasion and the wear rate reached 5.3×10−7 mm3/(m·N).Strengthening mechanisms such as dislocation pinning and the Hall−Petch theory,high hardness and the load transfer effect were crucial in determining the wear behavior of the Al5083−5wt.%B4C composite.On the other hand,the milled Al5083 sample represented a relatively high wear rate at 200°C,which seemed to be related to the local grain growth and a drop in its hardness.
基金financial support of the project from the National Natural Science Foundation of China (Nos. 51272206 and 51472198)the Program for Changjiang Scholars and Innovative Research Team in University (No. IRT1280)+2 种基金the National Key Laboratory Functional Composite (No. 9140C560109130C56201)the Fundamental Research Funds for the Central University (No. xkjc2014009)the State Key Laboratory for Mechanical Behavior of Materials (No. 20121207)
文摘A water-quenching technique has been adopted to evaluate thermal shock fracture and fatigue behaviors of porous Si3N4 ceramics in an air atmosphere. The high-porosity Si3N4 ceramics exhibit a higher strength retention and a better resistance to thermal shock fatigue because of its role of the pores as crack arresters.A dense and coherent surface oxide layer leads to a significant benefit in residual strength during thermal fatigue, however, an increased fatigue number to 30 th cycle cannot cause a further influence although a thicker oxide layer presents, which is attributed to holes defect and disappearance of part intergranular phase.
基金Project(50438010) supported by the National Natural Science Foundation of China
文摘Four-point bending tests were conducted up to failure on eleven reinforced concrete (RC) beams and strengthening beams to study the effectiveness of externally pouring ultra high toughness cementitious composites (UHTCC) on improving the flexural behavior of existing RC beams.The strengthening materials included UHTCC and high strength grade concrete.The parameters,such as thickness and length of strengthening layer and reinforcement in post-poured layer,were analyzed.The flexural behavior,failure mode and crack propagation of composite beams were investigated.The test results show that the strengthening layer improves the cracking and ultimate load by increasing the cross section area.Introducing UHTCC material into strengthening not only improves the bearing capacity of the original specimens,but also disperses larger cracks in upper concrete into multiple tightly-spaced fine cracks,thus prolonging the appearance of harm surface cracks and increasing the durability of existing structures.Compared with post-poured concrete,UHTCC is more suitable for working together with reinforcement.The load?deflection plots obtained from three-dimensional finite-element model (FEM) analyses are compared with those obtained from the experimental results,and show close correlation.