The influence of isothermal quenching process of low-alloy and medium carbon (LAMC) CrMnSi cast steel on the impact toughness was investigated. The microstructure and mechanical property of LAMC CrMnSi cast steel were...The influence of isothermal quenching process of low-alloy and medium carbon (LAMC) CrMnSi cast steel on the impact toughness was investigated. The microstructure and mechanical property of LAMC CrMnSi cast steel were analyzed by the laser optical modulator, the scanning electron microscopy, the energy dispersive spectrometer, the hardness and impact tests. The experimental results show that the dual phases of bainite and residual austenite can be obtained by the severity isothermal quenching, the fractographies of specimens change from quasi-cleavage to dimple at 310℃ for 60min, the impact toughness for specimens at the room temperature isothermally (achieves) 130J/cm^2, meantime and its hardness is more than 45(HRC).展开更多
基金Project(10541225) supported by the Ministry of Education of Heilongjiang Province
文摘The influence of isothermal quenching process of low-alloy and medium carbon (LAMC) CrMnSi cast steel on the impact toughness was investigated. The microstructure and mechanical property of LAMC CrMnSi cast steel were analyzed by the laser optical modulator, the scanning electron microscopy, the energy dispersive spectrometer, the hardness and impact tests. The experimental results show that the dual phases of bainite and residual austenite can be obtained by the severity isothermal quenching, the fractographies of specimens change from quasi-cleavage to dimple at 310℃ for 60min, the impact toughness for specimens at the room temperature isothermally (achieves) 130J/cm^2, meantime and its hardness is more than 45(HRC).