The structure, properties and application to water-soluble coatings of a new complex antimicrobial agent Ag-carboxylmethyl citosan-thiabendazole （Ag-CMCTS-TBZ） prepared from different materiel ratios were reported. ...The structure, properties and application to water-soluble coatings of a new complex antimicrobial agent Ag-carboxylmethyl citosan-thiabendazole （Ag-CMCTS-TBZ） prepared from different materiel ratios were reported. The silver ions were preferably coordinated with the free-NH2 groups and the -OH groups of secondary alcohol and carboxyl in CMCTS. TBZ preferably bonded to carboxyl group in CMCTS by electrostatic force and hydrogen bonding. Increase in silver ions content in the complex agent improved to some limited extent the antibacterial activity, but enhanced coloring and cost of the complex agent. Increase in TBZ content resulted in increase of antifungal activity, but decrease of water solubility of the complex agent. The antimicrobial MICs of the complex agent to Esherichia coil, Staphylococcus aureus, Candida albicans, Aspergillus niger, Mucor sp. were 20 -80, 15 -60, 20 - 55, 40 - 250, and 400 - 1700 mg/kg, respectively. Addition of 0.1% of this complex agent to acrylic emulsion paint made the paint without substantial change in color, luster, viscosity, odor or pH value, but with an excellent and chronically persisting broad-spectra antimicrobial activity.展开更多
Dental implants are the most common therapeutic approach for resolving tooth loss and damage.Despite technical advances in treatment,implant failure rates can be as high as 23%with the major cause of peri-implantitis:...Dental implants are the most common therapeutic approach for resolving tooth loss and damage.Despite technical advances in treatment,implant failure rates can be as high as 23%with the major cause of peri-implantitis:a multi-species bacterial infection.With an annual growth rate in implant placements of 8.78%per annum,implant failure caused by bacterial infection is a significant oral and general health issue.The rise in antibiotic resistance in oral bacteria further adds pressure to implant failure;thus,there is a need for adjunctive therapy to improve implant outcomes.Due to the broad spectrum of activity and a low risk of inducing bacterial resistance,peptide antibiotics are emerging as a promising implant coating material to reduce/prevent peri-implantitis and improve dental implant success rates.In this review,we summarised the current strategies of coating antimicrobial peptides(AMPs)onto dental implant material surfaces with multi-functional properties to enhance osteoblast growth and prevent bacterial infections.This review compared the recent reported literature on dental implant coating with AMPs,which will provide an overview of the current dental implant coating strategies using AMPs and insights for future clinical applications.展开更多
The inorganic antimicrobial material was inhibited to the microbes with the added metal ion,Zn.The primary wet product carrying 5%-10% zinc ion was generated under the following conditions：temperature was 95 ℃,solut...The inorganic antimicrobial material was inhibited to the microbes with the added metal ion,Zn.The primary wet product carrying 5%-10% zinc ion was generated under the following conditions：temperature was 95 ℃,solution zinc concentration was 1.2-2.0 mol/L,and the ratio of Zn solution to zeolite weight was 5：1.The final stable product was manufactured after baking in an oven for 1-3 h at the temperature of 500-900 ℃.The baked material was tested for its disinfection effectiveness and coloring effect when mixed with paint coating.Based on the final batch of tests,the zinc content of this anti-microbial product was further optimized.展开更多
The rapid in situ inhibition of bacterial contamination and subsequent infection without inducing drug resistance is highly vital for the successful implantation and long-term service of titanium(Ti)-based orthopedic ...The rapid in situ inhibition of bacterial contamination and subsequent infection without inducing drug resistance is highly vital for the successful implantation and long-term service of titanium(Ti)-based orthopedic implants.However,the instability and potential cytotoxicity of current coatings have deterred their clinical practice.In this study,anodic oxidized titania nanotubes(TNT)were modified with antibacterial polyhexamethylene guanidine(PG)with the assistance of 3,4-dihydroxyphenylacetic acid.Interestingly,the prepared TNT-PG coating exhibited superior in vitro antibacterial activity than flat Ti-PG coating and effectively killed typical pathogens such as Escherichia coli and superbug methicillinresistant Staphylococcus aureus with above 4-log reduction(>99.99%killed)in only 5 min.TNT-PG coating also exerted excellent hemocompatibility with red blood cells and nontoxicity toward mouse pre-osteoblasts(MC3 T3-E1)in 1 week of coculture.In addition,the efficient in vivo anti-infective property of this coating was observed in a rat subcutaneous infection model.More importantly,TNT-PG coating improved the expression of alkaline phosphatase and enhanced the extracellular matrix mineralization of pre-osteoblasts,denoting its osteoinductive capacity.This versatile TNT-PG coating with excellent antibacterial activity and biocompatibility could be a promising candidate for advanced orthopedic implant applications.展开更多
文摘The structure, properties and application to water-soluble coatings of a new complex antimicrobial agent Ag-carboxylmethyl citosan-thiabendazole （Ag-CMCTS-TBZ） prepared from different materiel ratios were reported. The silver ions were preferably coordinated with the free-NH2 groups and the -OH groups of secondary alcohol and carboxyl in CMCTS. TBZ preferably bonded to carboxyl group in CMCTS by electrostatic force and hydrogen bonding. Increase in silver ions content in the complex agent improved to some limited extent the antibacterial activity, but enhanced coloring and cost of the complex agent. Increase in TBZ content resulted in increase of antifungal activity, but decrease of water solubility of the complex agent. The antimicrobial MICs of the complex agent to Esherichia coil, Staphylococcus aureus, Candida albicans, Aspergillus niger, Mucor sp. were 20 -80, 15 -60, 20 - 55, 40 - 250, and 400 - 1700 mg/kg, respectively. Addition of 0.1% of this complex agent to acrylic emulsion paint made the paint without substantial change in color, luster, viscosity, odor or pH value, but with an excellent and chronically persisting broad-spectra antimicrobial activity.
基金National Health and Medical Research Council(NHMRC)of AustraliaNHMRC,Grant/Award Numbers:APP1142472,APP1158841,APP1185426+5 种基金ARC,Grant/Award Numbers:DP210102781,DP160101312,LE200100163Cancer Council Victoria,Grant/Award Number:APP1163284Australian Dental ResearchNHMRC Investigator,Grant/Award Number:APP2018256Shandong Provincial Hospital Affiliated to Shandong First Medical University,Grant/Award Number:2020FY027Natural Science Foundation of Shandong Province,Grant/Award Number:ZR2021QH333。
文摘Dental implants are the most common therapeutic approach for resolving tooth loss and damage.Despite technical advances in treatment,implant failure rates can be as high as 23%with the major cause of peri-implantitis:a multi-species bacterial infection.With an annual growth rate in implant placements of 8.78%per annum,implant failure caused by bacterial infection is a significant oral and general health issue.The rise in antibiotic resistance in oral bacteria further adds pressure to implant failure;thus,there is a need for adjunctive therapy to improve implant outcomes.Due to the broad spectrum of activity and a low risk of inducing bacterial resistance,peptide antibiotics are emerging as a promising implant coating material to reduce/prevent peri-implantitis and improve dental implant success rates.In this review,we summarised the current strategies of coating antimicrobial peptides(AMPs)onto dental implant material surfaces with multi-functional properties to enhance osteoblast growth and prevent bacterial infections.This review compared the recent reported literature on dental implant coating with AMPs,which will provide an overview of the current dental implant coating strategies using AMPs and insights for future clinical applications.
基金Funded by the Construct Plan of Cooperation Project from the Beijing Education Committee(No. XK100080432)
文摘The inorganic antimicrobial material was inhibited to the microbes with the added metal ion,Zn.The primary wet product carrying 5%-10% zinc ion was generated under the following conditions：temperature was 95 ℃,solution zinc concentration was 1.2-2.0 mol/L,and the ratio of Zn solution to zeolite weight was 5：1.The final stable product was manufactured after baking in an oven for 1-3 h at the temperature of 500-900 ℃.The baked material was tested for its disinfection effectiveness and coloring effect when mixed with paint coating.Based on the final batch of tests,the zinc content of this anti-microbial product was further optimized.
基金the National Key R&D Program of China(No.2018YFC1105402)the National Natural Science Foundation of China(No.21875189)+1 种基金the Key R&D Program of Jiangsu Province(No.BE201740)the Innovative Talents Promotion Project of Shaanxi Province(No.2019KJXX-064)。
文摘The rapid in situ inhibition of bacterial contamination and subsequent infection without inducing drug resistance is highly vital for the successful implantation and long-term service of titanium(Ti)-based orthopedic implants.However,the instability and potential cytotoxicity of current coatings have deterred their clinical practice.In this study,anodic oxidized titania nanotubes(TNT)were modified with antibacterial polyhexamethylene guanidine(PG)with the assistance of 3,4-dihydroxyphenylacetic acid.Interestingly,the prepared TNT-PG coating exhibited superior in vitro antibacterial activity than flat Ti-PG coating and effectively killed typical pathogens such as Escherichia coli and superbug methicillinresistant Staphylococcus aureus with above 4-log reduction(>99.99%killed)in only 5 min.TNT-PG coating also exerted excellent hemocompatibility with red blood cells and nontoxicity toward mouse pre-osteoblasts(MC3 T3-E1)in 1 week of coculture.In addition,the efficient in vivo anti-infective property of this coating was observed in a rat subcutaneous infection model.More importantly,TNT-PG coating improved the expression of alkaline phosphatase and enhanced the extracellular matrix mineralization of pre-osteoblasts,denoting its osteoinductive capacity.This versatile TNT-PG coating with excellent antibacterial activity and biocompatibility could be a promising candidate for advanced orthopedic implant applications.