为了研究液体横向射流在气膜作用下的破碎过程,采用背景光成像技术及VOF TO DPM方法进行了实验研究和仿真研究,模拟介质为水和空气.研究结果表明,液体射流在气膜作用下主要存在两种破碎过程:柱状破碎和表面破碎.Rayleigh-Taylor(R-T)不...为了研究液体横向射流在气膜作用下的破碎过程,采用背景光成像技术及VOF TO DPM方法进行了实验研究和仿真研究,模拟介质为水和空气.研究结果表明,液体射流在气膜作用下主要存在两种破碎过程:柱状破碎和表面破碎.Rayleigh-Taylor(R-T)不稳定性产生的表面波是液体射流发生柱状破碎的主要原因,气流穿透表面波的波谷导致射流柱破碎,破碎后的液丝沿流向逐渐发展呈带状分布.Kelvin-Helmholtz(K-H)不稳定性产生的表面波是液体射流发生表面破碎的主要原因,液丝和液滴从射流表面剥离.局部动量比对液体横向射流的破碎过程具有重要影响,当局部动量比较低时,液体射流的破碎由K-H不稳定性主导;随着局部动量比的增大液体射流的破碎逐渐由R-T不稳定性主导.液体射流的破碎长度及穿透深度均随局部动量比的增大而增大.展开更多
Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently, the service life of the liner made from traditional materials, such as Hadfield steel and alloyed s...Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently, the service life of the liner made from traditional materials, such as Hadfield steel and alloyed steels, is typically less than ten months. Bimetal liner, made from high Cr white cast iron and carbon steel, has been successfully developed by using liquid-liquid composite lost foam casting process. The microstructure and interface of the composite were analyzed using optical microscope, SEM, EDX and XRD. Micrographs indicate that the boundary of bimetal combination regions is staggered like dogtooth, two liquid metals are not mixed, and the interface presents excellent metallurgical bonding state. After heat treatment, the composite liner specimens have shown excellent properties, including hardness 〉 61 HRC, fracture toughness ak 〉16.5 J.cm2 and bending strength 〉1,600 MPa. Wear comparison was made between the bimetal composite liner and alloyed steel liner in an industrial hematite ball mill of WISCO, and the results of eight-month test in wet grinding environment have proved that the service life of the bimetal composite liner is three times as long as that of the alloyed steel liner.展开更多
文摘为了研究液体横向射流在气膜作用下的破碎过程,采用背景光成像技术及VOF TO DPM方法进行了实验研究和仿真研究,模拟介质为水和空气.研究结果表明,液体射流在气膜作用下主要存在两种破碎过程:柱状破碎和表面破碎.Rayleigh-Taylor(R-T)不稳定性产生的表面波是液体射流发生柱状破碎的主要原因,气流穿透表面波的波谷导致射流柱破碎,破碎后的液丝沿流向逐渐发展呈带状分布.Kelvin-Helmholtz(K-H)不稳定性产生的表面波是液体射流发生表面破碎的主要原因,液丝和液滴从射流表面剥离.局部动量比对液体横向射流的破碎过程具有重要影响,当局部动量比较低时,液体射流的破碎由K-H不稳定性主导;随着局部动量比的增大液体射流的破碎逐渐由R-T不稳定性主导.液体射流的破碎长度及穿透深度均随局部动量比的增大而增大.
基金supported by the National Natural Science Foundation of China under grant No.50805109the Fundamental Research Funds for the Central Universities under grant No.2011-1a-023
文摘Liners in wet ball mill for mineral processing industry must bear abrasive wear and corrosive wear, and consequently, the service life of the liner made from traditional materials, such as Hadfield steel and alloyed steels, is typically less than ten months. Bimetal liner, made from high Cr white cast iron and carbon steel, has been successfully developed by using liquid-liquid composite lost foam casting process. The microstructure and interface of the composite were analyzed using optical microscope, SEM, EDX and XRD. Micrographs indicate that the boundary of bimetal combination regions is staggered like dogtooth, two liquid metals are not mixed, and the interface presents excellent metallurgical bonding state. After heat treatment, the composite liner specimens have shown excellent properties, including hardness 〉 61 HRC, fracture toughness ak 〉16.5 J.cm2 and bending strength 〉1,600 MPa. Wear comparison was made between the bimetal composite liner and alloyed steel liner in an industrial hematite ball mill of WISCO, and the results of eight-month test in wet grinding environment have proved that the service life of the bimetal composite liner is three times as long as that of the alloyed steel liner.
