TiAl is diffusion bonded with Ti, TC4 Alloy and 40Cr Steel by heating in vacuum, and analysis of interfaces shows stratified Ti 3Al forms in TiAl/Ti interface closest to TiAl base, and the α phase and the α+β phase...TiAl is diffusion bonded with Ti, TC4 Alloy and 40Cr Steel by heating in vacuum, and analysis of interfaces shows stratified Ti 3Al forms in TiAl/Ti interface closest to TiAl base, and the α phase and the α+β phase arise closest to Ti base at lower temperature and higher temperature respectively; Structure of TiAl/TC4 interface is TiAl/γ+α 2/Ti 3Al/α-Ti/TC4 at lower temperature and TiAl/γ+β+α 2/TC4 at high temperature; in TiAl/40Cr steel interface, obvious decarbonised layer on steel side while TiC and reaction phase with Fe Al Ti system form on TiAl side.展开更多
TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase ...TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase arised closest to Ti base at 1173K and 1573K respectively. The phase structure of TiAl/ and the phase structure of TiAlwere observed be- tween AiAl and TC4 under respetive bonding temperature.The fiacture at tensile testing occurred in the bond - line, producing very flat fracture surfaces with some pull-out of the TiAl materials.The ultimate tensile strengths of the joint were approximate to γ-TiAl base marterial.展开更多
文摘TiAl is diffusion bonded with Ti, TC4 Alloy and 40Cr Steel by heating in vacuum, and analysis of interfaces shows stratified Ti 3Al forms in TiAl/Ti interface closest to TiAl base, and the α phase and the α+β phase arise closest to Ti base at lower temperature and higher temperature respectively; Structure of TiAl/TC4 interface is TiAl/γ+α 2/Ti 3Al/α-Ti/TC4 at lower temperature and TiAl/γ+β+α 2/TC4 at high temperature; in TiAl/40Cr steel interface, obvious decarbonised layer on steel side while TiC and reaction phase with Fe Al Ti system form on TiAl side.
文摘TiAl was diffusion bonded to Ti and TC4 alloy in vacuum furnace. Results showed,at the TiAl-Ti interface,the reaction layer of stratification Ti3Al was formed closest to TiAl base,and the a phase and the α + βphase arised closest to Ti base at 1173K and 1573K respectively. The phase structure of TiAl/ and the phase structure of TiAlwere observed be- tween AiAl and TC4 under respetive bonding temperature.The fiacture at tensile testing occurred in the bond - line, producing very flat fracture surfaces with some pull-out of the TiAl materials.The ultimate tensile strengths of the joint were approximate to γ-TiAl base marterial.