Graphene （G） was dispersed uniformly in water and used as an inhibitor in waterborne epoxy coatings. The effect of dispersed G on anticorrosion performance of epoxy coatings was evaluated. The composite coatings dis...Graphene （G） was dispersed uniformly in water and used as an inhibitor in waterborne epoxy coatings. The effect of dispersed G on anticorrosion performance of epoxy coatings was evaluated. The composite coatings displayed outstanding barrier properties against H20 molecule compared to the neat epoxy coating. Open circuit potential （OCP）, Tafel and electrochemical impedance spectroscopy （EIS） analysis confirmed that the corrosion rate exhibited by composite coatings with 0.5 wt% G was an order of magnitude lower than that of neat epoxy coating. Salt spray test results revealed superior corrosion resistance offered by the composite coating.展开更多
A phosphorus-containing bio-based epoxy resin(EADI)was synthesized from itaconic acid(IA)and 9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide(DOPO).As a matrix,its cured epoxy network with methyl hexahydrophthalic a...A phosphorus-containing bio-based epoxy resin(EADI)was synthesized from itaconic acid(IA)and 9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide(DOPO).As a matrix,its cured epoxy network with methyl hexahydrophthalic anhydride(MHHPA)as the curing agent showed comparable glass-transition temperature and mechanical properties to diglycidyl ether in a bisphenol A(DGEBA)system as well as good flame retardancy with UL94 V-0 grade during a vertical burning test.As a reactive flame retardant,its flame-resistant effect on DGEBA/MHHPA system as well as its influence on the curing behavior and the thermal and mechanical properties of the modified epoxy resin were investigated.Results showed that after the introduction of EADI,not only were the flame retardancy determined by vertical burning test,LOI measurement,and thermogravimetric analysis significantly improved,but also the curing reactivity,glass transition temperature(T g),initial degradation temperature for 5%weight loss(T d(5%)),and flexural modulus of the cured system improved as well.EADI has great potential to be used as a green flame retardant in epoxy resin systems.展开更多
基金supported by the National Natural Science Foundation of China (No.41506098)the China Postdoctoral Science Foundation (No.2015M580528)the Open Fund Project of Key Laboratory of Marine Materials and Related Technologies (No.LMMTKFKT-2014-008) in the Chinese Academy of Sciences
文摘Graphene （G） was dispersed uniformly in water and used as an inhibitor in waterborne epoxy coatings. The effect of dispersed G on anticorrosion performance of epoxy coatings was evaluated. The composite coatings displayed outstanding barrier properties against H20 molecule compared to the neat epoxy coating. Open circuit potential （OCP）, Tafel and electrochemical impedance spectroscopy （EIS） analysis confirmed that the corrosion rate exhibited by composite coatings with 0.5 wt% G was an order of magnitude lower than that of neat epoxy coating. Salt spray test results revealed superior corrosion resistance offered by the composite coating.
基金financially supported by the National Natural Science Foundation of China(51203176)the National Basic Research Program of China(2010CB631100)+3 种基金the Natural Science Foundation of Ningbo(2012A610095)the China Postdoctoral Science Foundation(2013M-540504)the Postdoctoral Science Foundation of Zhejiang Province(Bsh1201011)the Director Funds of the Ningbo Institute of Materials Technology and Engineering,Chinese Academy of Sciences(Y20224-QF06)
文摘A phosphorus-containing bio-based epoxy resin(EADI)was synthesized from itaconic acid(IA)and 9,10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide(DOPO).As a matrix,its cured epoxy network with methyl hexahydrophthalic anhydride(MHHPA)as the curing agent showed comparable glass-transition temperature and mechanical properties to diglycidyl ether in a bisphenol A(DGEBA)system as well as good flame retardancy with UL94 V-0 grade during a vertical burning test.As a reactive flame retardant,its flame-resistant effect on DGEBA/MHHPA system as well as its influence on the curing behavior and the thermal and mechanical properties of the modified epoxy resin were investigated.Results showed that after the introduction of EADI,not only were the flame retardancy determined by vertical burning test,LOI measurement,and thermogravimetric analysis significantly improved,but also the curing reactivity,glass transition temperature(T g),initial degradation temperature for 5%weight loss(T d(5%)),and flexural modulus of the cured system improved as well.EADI has great potential to be used as a green flame retardant in epoxy resin systems.