A computation framework for brittle fracture which incorporates weakest link statistics and a microme- chanics model reflecting reflecting local damage of the material is described.The Weibull stress W emerges as a ...A computation framework for brittle fracture which incorporates weakest link statistics and a microme- chanics model reflecting reflecting local damage of the material is described.The Weibull stress W emerges as a probabilistic fracture parameter to define the condition leading material failure. Unstable crack propa- gation occurs at a critical value of W which may be attained paior to or following some amount of duc- tile crack extension. A realistic model of ductile crack growth using the computation cell methodology is used to define the evolution of near tip stress fields during crack extension. An application of proposed framework to predict the measured geometry and ductile tearing effects on the statistical distributio of fracture toughness for the pipe line steel welded joint is described.展开更多
The rotation correction method of unloading compliance for a compact tensile （CT） specimen in the current J-integral resistance curves or critical J-integral test standards was under suspicion by tracing to its sour...The rotation correction method of unloading compliance for a compact tensile （CT） specimen in the current J-integral resistance curves or critical J-integral test standards was under suspicion by tracing to its source, and a new rotation correction method was proposed. The rotation center of the specimen is close to the crack tip, and the material constitutive relationship has little effect on the rotational radius R. If the formula for rotation correction recommended in current standards is used to measure the crack length of CT specimen, it will lead to larger error. A new formula with better accuracy for the crack length measurement of the CT specimen was presented.展开更多
The Impact toughness and fracture toughness of Austempered Ductile Iron (ADI) are described. The notched and un-notched Charpy impact toughness of ADI at room temperature are somewhat lower than that of steel castings...The Impact toughness and fracture toughness of Austempered Ductile Iron (ADI) are described. The notched and un-notched Charpy impact toughness of ADI at room temperature are somewhat lower than that of steel castings or forged steel pieces, however, they are approximately three times higher than that of normal pearlitic ductile iron. The impact toughness of ADI decreases with decreasing temperature; but at-40℃ it still maintains about 70% of the value at room temperature. The properties of fracture toughness are important in safety design and failure analysis. In this study all fracture toughness data of ADI are higher than that of conventional ductile iron, and are equivalent to or better than that of steel castings or forged steel pieces with the tensile strength equivalent to ADI.展开更多
文摘A computation framework for brittle fracture which incorporates weakest link statistics and a microme- chanics model reflecting reflecting local damage of the material is described.The Weibull stress W emerges as a probabilistic fracture parameter to define the condition leading material failure. Unstable crack propa- gation occurs at a critical value of W which may be attained paior to or following some amount of duc- tile crack extension. A realistic model of ductile crack growth using the computation cell methodology is used to define the evolution of near tip stress fields during crack extension. An application of proposed framework to predict the measured geometry and ductile tearing effects on the statistical distributio of fracture toughness for the pipe line steel welded joint is described.
基金supported by the National Natural Science Foundation of China (No. 11072205)
文摘The rotation correction method of unloading compliance for a compact tensile （CT） specimen in the current J-integral resistance curves or critical J-integral test standards was under suspicion by tracing to its source, and a new rotation correction method was proposed. The rotation center of the specimen is close to the crack tip, and the material constitutive relationship has little effect on the rotational radius R. If the formula for rotation correction recommended in current standards is used to measure the crack length of CT specimen, it will lead to larger error. A new formula with better accuracy for the crack length measurement of the CT specimen was presented.
文摘The Impact toughness and fracture toughness of Austempered Ductile Iron (ADI) are described. The notched and un-notched Charpy impact toughness of ADI at room temperature are somewhat lower than that of steel castings or forged steel pieces, however, they are approximately three times higher than that of normal pearlitic ductile iron. The impact toughness of ADI decreases with decreasing temperature; but at-40℃ it still maintains about 70% of the value at room temperature. The properties of fracture toughness are important in safety design and failure analysis. In this study all fracture toughness data of ADI are higher than that of conventional ductile iron, and are equivalent to or better than that of steel castings or forged steel pieces with the tensile strength equivalent to ADI.