Aluminum was leached out from coal fly ash by pressure acid-leaching method. The effects of coal fly ash size, sulfuric acid concentration, reaction time and reaction temperature on extraction efficiency of aluminum w...Aluminum was leached out from coal fly ash by pressure acid-leaching method. The effects of coal fly ash size, sulfuric acid concentration, reaction time and reaction temperature on extraction efficiency of aluminum were investigated comprehensively. The phase and morphology of coal fly ash and solid residues after reaction were analyzed by XRD, SEM and IR. The optimal technological conditions for extracting aluminum from coal fly ash were eventually confirmed that coal fly ash with size of 74 μm and sulfuric acid with concentration of 50% are mixed in pressure reaction kettle to react for 4 h at 180 ℃. Under the optimal conditions, the extraction efficiency of aluminum can reach 82.4%.展开更多
Alkali-leaching and acid-leaching were proposed for the dephosphorization of Changde iron ore, which contains an average of 1.12% for phosphorus content. Sodium hydroxide, sulfuriced, hydrochloric and nitric acids wer...Alkali-leaching and acid-leaching were proposed for the dephosphorization of Changde iron ore, which contains an average of 1.12% for phosphorus content. Sodium hydroxide, sulfuriced, hydrochloric and nitric acids were used for the preparation of leach solutions. The results show that phosphorus occurring as apatite phase could be removed by alkali-leaching, but those occurring in the iron phase could not. Sulfuric acid is the most effective among the three kinds of acid. 91.61% phosphorus removal was attained with 1% sulfuric acid after leaching for 20 rain at room temperature. Iron loss during acid-leaching can be negligible, which was less than 0.25%.The pH value of solution after leaching with1% sulfuric acid was about 0.86, which means acid would not be exhausted during the process and it could be recycled, and the recycle of sulfuric acid solution would make the dephosphorization process more economical.展开更多
The recovery of nickel from laterite ore with sulphuric acid under the effect of microwave irradiation was studied.The experimental results indicated that the extraction rate of nickel was influenced by reaction time,...The recovery of nickel from laterite ore with sulphuric acid under the effect of microwave irradiation was studied.The experimental results indicated that the extraction rate of nickel was influenced by reaction time,sulphuric acid concentration,and temperature,especially by microwave power.The results obtained from the experiments of orthogonal arrays showed that the optimum conditions of sulphuric acid concentration,reaction time,microwave power,and temperature were 25 vol.%,1.5 h,600 W,and 90°C,respectively.Under the optimal conditions,the nickel recovery could reach approximately 90.8%,which was higher than that obtained by conventional water bath heating.Kinetic experiments showed that the leaching of nickel in a sulphuric acid medium was controlled by chemical reaction occurring on the surface of laterite ore.The apparent activation energy was 38.9 kJ/mol.Microwave heating technology is efficient,clean,and easy to control and facilitate continuous processing of materials.展开更多
Proper treatment of acidleaching tailings(ALTs)of vanadiumbearing stone coal minerals is of great urgency.One approach is adding it into the raw materials during the preparation of lightweight aggregate(LWA).But clay ...Proper treatment of acidleaching tailings(ALTs)of vanadiumbearing stone coal minerals is of great urgency.One approach is adding it into the raw materials during the preparation of lightweight aggregate(LWA).But clay is always needed.In this paper,another solid waste,red mud,was mixed with ALTs as a source of flux components instead of clay.Evaluation of the physical characteristics,morphological structures,as well as crystal phases during the sintering process were investigated.When their mixtures with a proper ratio were sintered at 1080℃,a glassy phase with certain viscosity was formed,and the gases generated simultaneously were encapsulated by the melt.Finally,LWA with a onehour water absorption as low as 1.46%,a bulk density as low as 728.76 kgm 3 and a compressive strength as high as 10.77 MPa was fabricated.展开更多
基金Project (BO210(2008)) supported by the Foundation of "Hundred Talent Program" of Chinese Academic of SciencesProject (2008-G-158) supported by the Scientific and Technological Project of Qinghai Province, China
文摘Aluminum was leached out from coal fly ash by pressure acid-leaching method. The effects of coal fly ash size, sulfuric acid concentration, reaction time and reaction temperature on extraction efficiency of aluminum were investigated comprehensively. The phase and morphology of coal fly ash and solid residues after reaction were analyzed by XRD, SEM and IR. The optimal technological conditions for extracting aluminum from coal fly ash were eventually confirmed that coal fly ash with size of 74 μm and sulfuric acid with concentration of 50% are mixed in pressure reaction kettle to react for 4 h at 180 ℃. Under the optimal conditions, the extraction efficiency of aluminum can reach 82.4%.
基金Project (50321402) supported by the National Natural Science Foundation of China project(2004CB619204) supported by Major State Basic Research Development Program of China
文摘Alkali-leaching and acid-leaching were proposed for the dephosphorization of Changde iron ore, which contains an average of 1.12% for phosphorus content. Sodium hydroxide, sulfuriced, hydrochloric and nitric acids were used for the preparation of leach solutions. The results show that phosphorus occurring as apatite phase could be removed by alkali-leaching, but those occurring in the iron phase could not. Sulfuric acid is the most effective among the three kinds of acid. 91.61% phosphorus removal was attained with 1% sulfuric acid after leaching for 20 rain at room temperature. Iron loss during acid-leaching can be negligible, which was less than 0.25%.The pH value of solution after leaching with1% sulfuric acid was about 0.86, which means acid would not be exhausted during the process and it could be recycled, and the recycle of sulfuric acid solution would make the dephosphorization process more economical.
文摘The recovery of nickel from laterite ore with sulphuric acid under the effect of microwave irradiation was studied.The experimental results indicated that the extraction rate of nickel was influenced by reaction time,sulphuric acid concentration,and temperature,especially by microwave power.The results obtained from the experiments of orthogonal arrays showed that the optimum conditions of sulphuric acid concentration,reaction time,microwave power,and temperature were 25 vol.%,1.5 h,600 W,and 90°C,respectively.Under the optimal conditions,the nickel recovery could reach approximately 90.8%,which was higher than that obtained by conventional water bath heating.Kinetic experiments showed that the leaching of nickel in a sulphuric acid medium was controlled by chemical reaction occurring on the surface of laterite ore.The apparent activation energy was 38.9 kJ/mol.Microwave heating technology is efficient,clean,and easy to control and facilitate continuous processing of materials.
文摘Proper treatment of acidleaching tailings(ALTs)of vanadiumbearing stone coal minerals is of great urgency.One approach is adding it into the raw materials during the preparation of lightweight aggregate(LWA).But clay is always needed.In this paper,another solid waste,red mud,was mixed with ALTs as a source of flux components instead of clay.Evaluation of the physical characteristics,morphological structures,as well as crystal phases during the sintering process were investigated.When their mixtures with a proper ratio were sintered at 1080℃,a glassy phase with certain viscosity was formed,and the gases generated simultaneously were encapsulated by the melt.Finally,LWA with a onehour water absorption as low as 1.46%,a bulk density as low as 728.76 kgm 3 and a compressive strength as high as 10.77 MPa was fabricated.