The effect of Zn on the microstructure, the mechanical property and the corrosion property in simulated body fluid(SBF) of an extruded Mg-Mn alloy was studied. The results indicate that the addition of Zn element can ...The effect of Zn on the microstructure, the mechanical property and the corrosion property in simulated body fluid(SBF) of an extruded Mg-Mn alloy was studied. The results indicate that the addition of Zn element can significantly refine the grain size of the extruded Mg-Mn alloy. When Zn content is increased from 0% to 3%, the grain size decreases from 12 μm to 4 μm. Meanwhile, the mechanical properties also increase remarkably with increasing Zn content. When Zn content is 3%, the ultimate tensile strength and the yield strength are increased by 54.7 MPa and 69.7 MPa, respectively. Zn can also improve the anti-corrosion property of the alloy. The best anti-corrosion property is obtained with 1% Zn. However, further increase of Zn content up to 3% deteriorates the corrosion property. Finally, the influence mechanism of Zn on the microstructure, the mechanical property and the corrosion property was discussed.展开更多
AZ80 magnesium alloy was prepared by hot extrusion of recycled machined chips and its microstructure and mechanical properties were investigated. Hot pressing was employed to prepare extrusion billets of AZ80 chips, t...AZ80 magnesium alloy was prepared by hot extrusion of recycled machined chips and its microstructure and mechanical properties were investigated. Hot pressing was employed to prepare extrusion billets of AZ80 chips, then the billets were hot extruded at 623 K with an extrusion ratio of 25∶1. The extruded rods show a high ultimate tensile strength of 285 MPa and a high elongation of 6%. Due to grain refinement by extrusion, mechanical properties of the extruded rods are much higher than those of as-cast AZ80 alloy. Process technique and chips densification mechanism were also studied. Results show that hot extrusion is an efficient method for AZ80 alloy chips recycling.展开更多
基金Project supported by Hundreds Talent Program of Chinese Academy of Sciences and Shenyang Sciences and Technology Program
文摘The effect of Zn on the microstructure, the mechanical property and the corrosion property in simulated body fluid(SBF) of an extruded Mg-Mn alloy was studied. The results indicate that the addition of Zn element can significantly refine the grain size of the extruded Mg-Mn alloy. When Zn content is increased from 0% to 3%, the grain size decreases from 12 μm to 4 μm. Meanwhile, the mechanical properties also increase remarkably with increasing Zn content. When Zn content is 3%, the ultimate tensile strength and the yield strength are increased by 54.7 MPa and 69.7 MPa, respectively. Zn can also improve the anti-corrosion property of the alloy. The best anti-corrosion property is obtained with 1% Zn. However, further increase of Zn content up to 3% deteriorates the corrosion property. Finally, the influence mechanism of Zn on the microstructure, the mechanical property and the corrosion property was discussed.
文摘AZ80 magnesium alloy was prepared by hot extrusion of recycled machined chips and its microstructure and mechanical properties were investigated. Hot pressing was employed to prepare extrusion billets of AZ80 chips, then the billets were hot extruded at 623 K with an extrusion ratio of 25∶1. The extruded rods show a high ultimate tensile strength of 285 MPa and a high elongation of 6%. Due to grain refinement by extrusion, mechanical properties of the extruded rods are much higher than those of as-cast AZ80 alloy. Process technique and chips densification mechanism were also studied. Results show that hot extrusion is an efficient method for AZ80 alloy chips recycling.