A series of catalysts with (Ce-Zr-La-Pr)O contents range from 0 to 50% in coating and single-palladium loads on substrates were prepared to study effects of (Ce-Zr-La-Pr)O contents on catalytic activities and durabili...A series of catalysts with (Ce-Zr-La-Pr)O contents range from 0 to 50% in coating and single-palladium loads on substrates were prepared to study effects of (Ce-Zr-La-Pr)O contents on catalytic activities and durability by contrasting the characteristics of light-off, A/F and catalytic conversions of the fresh catalysts with that of the aged catalysts. The results show that (Ce-Zr-La-Pr)O can enhance the catalysts light-off characteristics, widen A/F windows and increase catalytic conversions at a certain extent through optimizing physical structural and chemical property of the mixed coating. However, (Ce-Zr-La-Pr)O contents influence greatly on the catalysts activities and durability, and the catalysts with contents ranging from 10% to 30% exhibited better integrative properties in all samples, and 10% was the optical content to make the catalyst performance highest in this thesis. It is indicated that an suitable content of (Ce-Zr-La-Pr)O plays an important role in assisting catalysis, enhancing durability and increasing oxygen storage capability.展开更多
Important effects exist between precious metals and rare earths oxides in three-way catalyst, especially the coordinated effects. These effects were studied by using H2PtCl6, Pt(NH3)2(NO2)2 and Pt(OH)2(C2H5ONH2)2 as P...Important effects exist between precious metals and rare earths oxides in three-way catalyst, especially the coordinated effects. These effects were studied by using H2PtCl6, Pt(NH3)2(NO2)2 and Pt(OH)2(C2H5ONH2)2 as Pt precursors, and the mixed oxide of (Ce-Zr-La-Pr)O as base material to prepare a series of catalysts, and their performances of the catalysts were studied by TPR and CO pulse titration technologies. The results shown that Pt precursors and their solutions pH values influenced the oxygen storage capabilities, the active metal distribution degrees of the catalysts obviously, and every catalyst prepared by different precursors had an optimal pH values. It indicates that the active metals precursors and their solutions acidities have outstanding influences on the catalysts performances for the mutual effects existing between the active metals and the Rare Earth metal oxides, which results from the mate groups of the precursors and the solution acidity.展开更多
文摘A series of catalysts with (Ce-Zr-La-Pr)O contents range from 0 to 50% in coating and single-palladium loads on substrates were prepared to study effects of (Ce-Zr-La-Pr)O contents on catalytic activities and durability by contrasting the characteristics of light-off, A/F and catalytic conversions of the fresh catalysts with that of the aged catalysts. The results show that (Ce-Zr-La-Pr)O can enhance the catalysts light-off characteristics, widen A/F windows and increase catalytic conversions at a certain extent through optimizing physical structural and chemical property of the mixed coating. However, (Ce-Zr-La-Pr)O contents influence greatly on the catalysts activities and durability, and the catalysts with contents ranging from 10% to 30% exhibited better integrative properties in all samples, and 10% was the optical content to make the catalyst performance highest in this thesis. It is indicated that an suitable content of (Ce-Zr-La-Pr)O plays an important role in assisting catalysis, enhancing durability and increasing oxygen storage capability.
基金Project supported by the National High Technology Research and Development Programs (863 ) of China (2002 AA321060, 2004AA649040) Yunnan Province Science Technology Program (2004B0028Q)
文摘Important effects exist between precious metals and rare earths oxides in three-way catalyst, especially the coordinated effects. These effects were studied by using H2PtCl6, Pt(NH3)2(NO2)2 and Pt(OH)2(C2H5ONH2)2 as Pt precursors, and the mixed oxide of (Ce-Zr-La-Pr)O as base material to prepare a series of catalysts, and their performances of the catalysts were studied by TPR and CO pulse titration technologies. The results shown that Pt precursors and their solutions pH values influenced the oxygen storage capabilities, the active metal distribution degrees of the catalysts obviously, and every catalyst prepared by different precursors had an optimal pH values. It indicates that the active metals precursors and their solutions acidities have outstanding influences on the catalysts performances for the mutual effects existing between the active metals and the Rare Earth metal oxides, which results from the mate groups of the precursors and the solution acidity.