Electrochemical corrosion behavior of Nd-Fe-B sintered magnets in nitric acid, hydrochloric acid, sulfuric acid, phosphate acid and in oxalic acid was studied. Potentiodynamic polarization curves and immersion time de...Electrochemical corrosion behavior of Nd-Fe-B sintered magnets in nitric acid, hydrochloric acid, sulfuric acid, phosphate acid and in oxalic acid was studied. Potentiodynamic polarization curves and immersion time dependence of corrosion rates of Nd-Fe-B sintered magnets in different acid solutions were tested. Microstructures of corroded Nd-Fe-B sintered magnets were investigated by means of SEM and AFM. The results indicate that in strong acid solutions of similar hydrogen ion concentration, the corrosion current increases in the order of HCl 〉 H3SO4 〉 HNO3 solution and Nd-Fe-B sintered magnets are passivated in phosphate acid and oxalic acid. Within 25 min, the corrosion rates of Nd-Fe-B sintered magnets in H2SO4 and H3PO4 solutions show a declining trend with immersion time, while in HNO3 and HCl solutions the corrosion rates are rising. And in H2C2O4 solution, weight of the magnets increases. The brim of Nd-Fe-B sintered magnets is corroded rather seriously and the size of the magnets changed greatly in nitric acid. The surfaces of the corroded magnets in the above mentioned acid solutions are all coarse.展开更多
A series of rare earth compound oxides with the formula of La0.8Sr0.2Mn1-xCoxO3（ were prepared by the method of citric acid. Structures, figures and magnetic properties of the x=0.0, 0.3, 0.5, 1.0） samples were anal...A series of rare earth compound oxides with the formula of La0.8Sr0.2Mn1-xCoxO3（ were prepared by the method of citric acid. Structures, figures and magnetic properties of the x=0.0, 0.3, 0.5, 1.0） samples were analyzed by means of XRD, SEM and SQUID. Experiment results prove that all the samples are hexagonal, but their figures and magnetic properties are different. La0.8Sr0.2MnO3 is ferromagnetic. La0.8Sr0.2Mn0.7CO0.3O3 and La0.8Sr0.2Mn0.5Co0.5O3 are ferrimagnetic. La0.8Sr0.2CoO3 is antiferromagnetic. SEM results indicate that the structure of the first three are three-dimensional reticulations which are made up of some small ellipsoids which link up at the head and the end. The fourth sample looks like some dispersed small balls.展开更多
Adsorption,absorption and diffusion pathways of nitrogen are studied for ferromagnetic body-centered cubic iron via spin-polarized density functional theory in combination with the climbing image nudged elastic band m...Adsorption,absorption and diffusion pathways of nitrogen are studied for ferromagnetic body-centered cubic iron via spin-polarized density functional theory in combination with the climbing image nudged elastic band method.The computed data suggest that,depending on the coverage of N atoms,N prefers to stay on particular surface sites.Once pinned down well below the surface,N prefers to move into octahedral interstices rather than tetrahedral interstices.However,the tetrahedral interstices are crucial because they act as transition states and yield the saddle point energies of the corresponding minimum energy pathways.In comparison with carbon,we found that nitrogen prefers a different pathway from the(1 0 0)surface to the subsurface due to its strong repulsive interaction with Fe ions.展开更多
文摘Electrochemical corrosion behavior of Nd-Fe-B sintered magnets in nitric acid, hydrochloric acid, sulfuric acid, phosphate acid and in oxalic acid was studied. Potentiodynamic polarization curves and immersion time dependence of corrosion rates of Nd-Fe-B sintered magnets in different acid solutions were tested. Microstructures of corroded Nd-Fe-B sintered magnets were investigated by means of SEM and AFM. The results indicate that in strong acid solutions of similar hydrogen ion concentration, the corrosion current increases in the order of HCl 〉 H3SO4 〉 HNO3 solution and Nd-Fe-B sintered magnets are passivated in phosphate acid and oxalic acid. Within 25 min, the corrosion rates of Nd-Fe-B sintered magnets in H2SO4 and H3PO4 solutions show a declining trend with immersion time, while in HNO3 and HCl solutions the corrosion rates are rising. And in H2C2O4 solution, weight of the magnets increases. The brim of Nd-Fe-B sintered magnets is corroded rather seriously and the size of the magnets changed greatly in nitric acid. The surfaces of the corroded magnets in the above mentioned acid solutions are all coarse.
文摘A series of rare earth compound oxides with the formula of La0.8Sr0.2Mn1-xCoxO3（ were prepared by the method of citric acid. Structures, figures and magnetic properties of the x=0.0, 0.3, 0.5, 1.0） samples were analyzed by means of XRD, SEM and SQUID. Experiment results prove that all the samples are hexagonal, but their figures and magnetic properties are different. La0.8Sr0.2MnO3 is ferromagnetic. La0.8Sr0.2Mn0.7CO0.3O3 and La0.8Sr0.2Mn0.5Co0.5O3 are ferrimagnetic. La0.8Sr0.2CoO3 is antiferromagnetic. SEM results indicate that the structure of the first three are three-dimensional reticulations which are made up of some small ellipsoids which link up at the head and the end. The fourth sample looks like some dispersed small balls.
基金financial support from the National Basic Research Program of China(973 Program,Grant No.2012CB932202)the National Natural Science Foundation of China(Grant Nos.50890174,50971088 and 51071102)
文摘Adsorption,absorption and diffusion pathways of nitrogen are studied for ferromagnetic body-centered cubic iron via spin-polarized density functional theory in combination with the climbing image nudged elastic band method.The computed data suggest that,depending on the coverage of N atoms,N prefers to stay on particular surface sites.Once pinned down well below the surface,N prefers to move into octahedral interstices rather than tetrahedral interstices.However,the tetrahedral interstices are crucial because they act as transition states and yield the saddle point energies of the corresponding minimum energy pathways.In comparison with carbon,we found that nitrogen prefers a different pathway from the(1 0 0)surface to the subsurface due to its strong repulsive interaction with Fe ions.