The cracking of coatings and the deformation of base frustrate the application of laser cladding technology especially on surface of the ring circular orbit.In order to solve the two problems above,the stress and stra...The cracking of coatings and the deformation of base frustrate the application of laser cladding technology especially on surface of the ring circular orbit.In order to solve the two problems above,the stress and strain fields of the laser cladding process on the ring circular orbit were analyzed through the finite-element method,based on the temperature field.The wedge module of the ring circular ring was the subject investigated. The calculating results show that during the cladding process the crank point tends to generate the transversal crack;the centre point on the coating/base interface tends to generate longitudinal crack;the intersecting edge of the coating and base tends to generate toe crack.Moreover,the cracking tendency of the outer marginal point is obviously greater than that of the inner marginal point.The rather high stress appears at the border position where the constraint exists,and the stress on the point in front of molten pool under the range of laser irradiation is large as well.And the displacement becomes larger as the cladding process proceeds.展开更多
The phase diagrams of the Li2MoO4-Na2MoO4 and Na2MoO4-K2MoO4 systems have been reassessed using differential thermal analysis together with high-temperature and room-temperature X-ray diffraction analysis. The results...The phase diagrams of the Li2MoO4-Na2MoO4 and Na2MoO4-K2MoO4 systems have been reassessed using differential thermal analysis together with high-temperature and room-temperature X-ray diffraction analysis. The results showed that the compound Li2MoO4·6Na2MoO4 did not exist; however,it confirmed the existence of the compound Li2MoO4·3Na2MoO4 in the Li2MoO4-Na2MoO4 systems. With regard to the system of Na2MoO4-K2MoO4,we could not confirm the results reported by Bukhanova who claimed that the system was eutectic type with 1∶1 and 1∶2 intermediate compounds,refuting the statement of Amadori who thought there was an apparent phase boundary at high temperature in α-solid solution region of the Na2MoO4-K2MoO4 binary system. The revised phase diagrams of these systems are illustrated in this article. These experimental results are in agreement with the computerized prediction using the support vector machine-atomic parameter method for the assessment of phase diagrams.展开更多
文摘The cracking of coatings and the deformation of base frustrate the application of laser cladding technology especially on surface of the ring circular orbit.In order to solve the two problems above,the stress and strain fields of the laser cladding process on the ring circular orbit were analyzed through the finite-element method,based on the temperature field.The wedge module of the ring circular ring was the subject investigated. The calculating results show that during the cladding process the crank point tends to generate the transversal crack;the centre point on the coating/base interface tends to generate longitudinal crack;the intersecting edge of the coating and base tends to generate toe crack.Moreover,the cracking tendency of the outer marginal point is obviously greater than that of the inner marginal point.The rather high stress appears at the border position where the constraint exists,and the stress on the point in front of molten pool under the range of laser irradiation is large as well.And the displacement becomes larger as the cladding process proceeds.
文摘The phase diagrams of the Li2MoO4-Na2MoO4 and Na2MoO4-K2MoO4 systems have been reassessed using differential thermal analysis together with high-temperature and room-temperature X-ray diffraction analysis. The results showed that the compound Li2MoO4·6Na2MoO4 did not exist; however,it confirmed the existence of the compound Li2MoO4·3Na2MoO4 in the Li2MoO4-Na2MoO4 systems. With regard to the system of Na2MoO4-K2MoO4,we could not confirm the results reported by Bukhanova who claimed that the system was eutectic type with 1∶1 and 1∶2 intermediate compounds,refuting the statement of Amadori who thought there was an apparent phase boundary at high temperature in α-solid solution region of the Na2MoO4-K2MoO4 binary system. The revised phase diagrams of these systems are illustrated in this article. These experimental results are in agreement with the computerized prediction using the support vector machine-atomic parameter method for the assessment of phase diagrams.