W-Y2O3 composite nanopowders prepared via wet chemical method exhibit unique morphologies and micro structures.The yttrium addition during chemical reaction process affects not only the composition of tungsten acid hy...W-Y2O3 composite nanopowders prepared via wet chemical method exhibit unique morphologies and micro structures.The yttrium addition during chemical reaction process affects not only the composition of tungsten acid hydrate precursors,but also the reduction property of tungsten oxide transformed from precursors.In this study,the morphology evolution of the samples with and without yttrium during reduction process has been studied,and it is found that the addition of yttrium can exert a strong influence on the reduction route of tungsten oxide and the final morphology of tungsten particles.The cause of the difference of reduction route and tungsten particle morphology is also analyzed.It is suggested that the composition of the samples with yttrium at the beginning of reduction is pure cubic system WO3(c-WO3),and the c-WO3 particles have c-WO3 whiskers attached to the surface.This kind of whiskers is essential for c-WO3 to be reduced directly to tungsten and also helpful to obtain W-Y2O3 powders with small size and good uniformity.展开更多
A fluidized bed jet milling process was used to make micro-fine high Nb-containing TiAl alloyed powders from the chippings obtained by crushing the Ti-45Al-8.5Nb-(W,B,Y) ingot.The influences of classifier frequency on...A fluidized bed jet milling process was used to make micro-fine high Nb-containing TiAl alloyed powders from the chippings obtained by crushing the Ti-45Al-8.5Nb-(W,B,Y) ingot.The influences of classifier frequency on powder characteristics were investigated.The results show that the powders with controlled average particle size can be prepared on a large scale.The powders with different sizes are all dominated by γ with aminor amount of α2-Ti3Al.The particle size significantly decreases with the classifier frequency increasing.At a classifier frequency higher than 38 Hz,the average particle size of the ground powders is lower than 25μm.The powders are composed of two differ-ent sizes of particles:shaped particles and some clastic particles,and both particle sizes meet the log-normal distribution.With the classifier frequency increasing,the both sizes decrease;meanwhile,the proportion of the clastic particles gradually increases,and the size distribution span value of the ground powders increases correspondingly.展开更多
Monodisperse Fe-based and Co-based nanopar-ticles exhibit unique magnetic properties. They play important roles in magnetic storage and biomedical application. Their chemical synthesis and performance enhancement draw...Monodisperse Fe-based and Co-based nanopar-ticles exhibit unique magnetic properties. They play important roles in magnetic storage and biomedical application. Their chemical synthesis and performance enhancement draw a lot of study interest. Investigations of magnetic metallic nano-particles are very active in many scientific fields. This paper reviews the present advances in chemical synthesis, perfor-mance enhancement, and potential applications of monodis-perse Fe-based and Co-based nanoparticles.展开更多
SmOHCO3micro/nano particles were prepared in water/oil （W/O） reverse microemulsion composed of cetyltrimethyl ammonium bromide （CTAB）, n-octane, n-butanol, Sm（NO3）3·6H2O and urea aqueous solution by the cou...SmOHCO3micro/nano particles were prepared in water/oil （W/O） reverse microemulsion composed of cetyltrimethyl ammonium bromide （CTAB）, n-octane, n-butanol, Sm（NO3）3·6H2O and urea aqueous solution by the coupling route of homogeneous precipitation with microemulsion. The nanoparticles were characterized and analyzed by X-ray powder diffraction （XRD）, thermal gravimetric and differential thermal gravimetric analysis （TG-DTG）, Fourier transform infrared absorption spectra （FT-IR） and scan-ning electron microscope （SEM）. The results showed that the phase SmOHCO3 micro/nano particles was in agreement with pure or-thorhombic phase. The different morphologies of SmOHCO3 micro/nano particles with good monodispersity and size were obtained by regulating the reaction temperature and reaction time. Possible formation mechanisms of the morphological structure of SmO-HCO3 were proposed and discussed.展开更多
Cu-Ni alloy nanoparticles were prepared by a microwave combustion method with the molar ratios of CU2＋ to Ni2＋ as 3：7, 4：6, 5：5, 6：4 and 7：3. The as-prepared samples were characterized by XRD, HR-SEM, EDX and V...Cu-Ni alloy nanoparticles were prepared by a microwave combustion method with the molar ratios of CU2＋ to Ni2＋ as 3：7, 4：6, 5：5, 6：4 and 7：3. The as-prepared samples were characterized by XRD, HR-SEM, EDX and VSM. XRD and EDX analyses suggest the formation of pure alloy powders. The average crystallite sizes were found to be in the range of 21.56-33.25 nm. HR-SEM images show the clustered/agglomerated particle-like morphology structure. VSM results reveal that for low Ni content （CusNis, Cu6Ni4 and Cu7Ni3）, the system shows paramagnetic behaviors, whereas for high Ni content （Cu3Ni7 and Cu4Ni6）, it becomes ferromagnetic.展开更多
SnSb2S4 thin films were prepared from powder by thermal evaporation under vacuum of 1.33 × 10^-4 Pa （ 10^-6 Torr） on unheated glass substrates. The effect of thickness on the structural, morphological and optic...SnSb2S4 thin films were prepared from powder by thermal evaporation under vacuum of 1.33 × 10^-4 Pa （ 10^-6 Torr） on unheated glass substrates. The effect of thickness on the structural, morphological and optical properties of SnSb2S4 thin films was investigated. Films thickness measured by interference fringes method varied from 50 to 700 nm. X-ray diffraction analysis revealed that all the SnSb2S4 films were polycrystalline in spite without heating the substrates and the crystallinity was improved with increasing film thickness. The microstructure parameters： crystallite size, strain and dislocation density were calculated. It was observed that the crystallite size increased and the crystal defects decreased with increasing film thickness. In addition, by increasing the film thickness, an enhancement in the surface roughness root-mean-square （RMS） increased from 2.0 to 6.6 nm. The fundamental optical parameters like band gap, absorption and extinction coefficient were calculated in the strong absorption region of transmittance and reflectance spectrum. The optical absorption measurements indicated that the band （Eg） gap of the thin films decreased from 2.10 to 1.65 eV with increasing film thickness. The refractive indexes were evaluated in transparent region in terms of envelope method, which was suggested by Swanepoul. It was observed that the refractive index increased with increasing film thickness.展开更多
利用溶胶-凝胶法在La Ni O3/Si O2/Si衬底上制备了掺Mn量为0%、1%、5%、10%（质量分数）的0.7Bi Fe O3-0.3Pb Ti O3（BFMPT7030/x,x=0,0.01,0.05,0.1）薄膜。XRD测试表明,薄膜均完全结晶,呈现高度（100）择优取向。通过对薄膜晶体结构分...利用溶胶-凝胶法在La Ni O3/Si O2/Si衬底上制备了掺Mn量为0%、1%、5%、10%（质量分数）的0.7Bi Fe O3-0.3Pb Ti O3（BFMPT7030/x,x=0,0.01,0.05,0.1）薄膜。XRD测试表明,薄膜均完全结晶,呈现高度（100）择优取向。通过对薄膜晶体结构分析,发现BFMPT7030/0.05薄膜具有最小的晶粒尺寸（258 nm）及最小的晶胞体积（61.25×10-3 nm3）。SEM测试结果显示样品晶粒生长充分,晶粒尺寸在150~300 nm之间。铁电性能测试结果表明,当Mn含量为5%时,铁电性能较好,电滞回线形状最好,最为饱和。漏电流测试结果表明随着掺Mn量增加,BFMPT7030薄膜的漏电流随电场增大而增加的趋势减弱。展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51822404 and 51574178)the Science and Technology Program of Tianjin(No.18YFZCGX00070)+1 种基金the Natural Science Foundation of Tianjin(No.18JCYBJC17900)the Seed Foundation of Tianjin University(Nos.2018XRX-0005 and 2019XYF-0066).
文摘W-Y2O3 composite nanopowders prepared via wet chemical method exhibit unique morphologies and micro structures.The yttrium addition during chemical reaction process affects not only the composition of tungsten acid hydrate precursors,but also the reduction property of tungsten oxide transformed from precursors.In this study,the morphology evolution of the samples with and without yttrium during reduction process has been studied,and it is found that the addition of yttrium can exert a strong influence on the reduction route of tungsten oxide and the final morphology of tungsten particles.The cause of the difference of reduction route and tungsten particle morphology is also analyzed.It is suggested that the composition of the samples with yttrium at the beginning of reduction is pure cubic system WO3(c-WO3),and the c-WO3 particles have c-WO3 whiskers attached to the surface.This kind of whiskers is essential for c-WO3 to be reduced directly to tungsten and also helpful to obtain W-Y2O3 powders with small size and good uniformity.
基金financially supported by the National Nature Science Foundation of China (No.50974017)
文摘A fluidized bed jet milling process was used to make micro-fine high Nb-containing TiAl alloyed powders from the chippings obtained by crushing the Ti-45Al-8.5Nb-(W,B,Y) ingot.The influences of classifier frequency on powder characteristics were investigated.The results show that the powders with controlled average particle size can be prepared on a large scale.The powders with different sizes are all dominated by γ with aminor amount of α2-Ti3Al.The particle size significantly decreases with the classifier frequency increasing.At a classifier frequency higher than 38 Hz,the average particle size of the ground powders is lower than 25μm.The powders are composed of two differ-ent sizes of particles:shaped particles and some clastic particles,and both particle sizes meet the log-normal distribution.With the classifier frequency increasing,the both sizes decrease;meanwhile,the proportion of the clastic particles gradually increases,and the size distribution span value of the ground powders increases correspondingly.
基金partially supported by the National Basic Research Program of China(No.2012CB932702)the National Natural Science Foundation of China(Nos.51071022,51271020,and 11174031)+3 种基金the Program for Changjiang Scholars and Innovative Research Teams in University(PCSIRT)Beijing Nova Program(No.2011031)the Fundamental Research Funds for the Central Universitiesthe State Key Laboratory of Advanced Metals and Materials(No.2011-Z03)
文摘Monodisperse Fe-based and Co-based nanopar-ticles exhibit unique magnetic properties. They play important roles in magnetic storage and biomedical application. Their chemical synthesis and performance enhancement draw a lot of study interest. Investigations of magnetic metallic nano-particles are very active in many scientific fields. This paper reviews the present advances in chemical synthesis, perfor-mance enhancement, and potential applications of monodis-perse Fe-based and Co-based nanoparticles.
基金Project supported by the grant from Scientific and Technological Projects in Shaanxi Province(2011K07-23)Shaanxi Provincial Department of Education Special Research Projects(11JK0566)
文摘SmOHCO3micro/nano particles were prepared in water/oil （W/O） reverse microemulsion composed of cetyltrimethyl ammonium bromide （CTAB）, n-octane, n-butanol, Sm（NO3）3·6H2O and urea aqueous solution by the coupling route of homogeneous precipitation with microemulsion. The nanoparticles were characterized and analyzed by X-ray powder diffraction （XRD）, thermal gravimetric and differential thermal gravimetric analysis （TG-DTG）, Fourier transform infrared absorption spectra （FT-IR） and scan-ning electron microscope （SEM）. The results showed that the phase SmOHCO3 micro/nano particles was in agreement with pure or-thorhombic phase. The different morphologies of SmOHCO3 micro/nano particles with good monodispersity and size were obtained by regulating the reaction temperature and reaction time. Possible formation mechanisms of the morphological structure of SmO-HCO3 were proposed and discussed.
文摘Cu-Ni alloy nanoparticles were prepared by a microwave combustion method with the molar ratios of CU2＋ to Ni2＋ as 3：7, 4：6, 5：5, 6：4 and 7：3. The as-prepared samples were characterized by XRD, HR-SEM, EDX and VSM. XRD and EDX analyses suggest the formation of pure alloy powders. The average crystallite sizes were found to be in the range of 21.56-33.25 nm. HR-SEM images show the clustered/agglomerated particle-like morphology structure. VSM results reveal that for low Ni content （CusNis, Cu6Ni4 and Cu7Ni3）, the system shows paramagnetic behaviors, whereas for high Ni content （Cu3Ni7 and Cu4Ni6）, it becomes ferromagnetic.
文摘SnSb2S4 thin films were prepared from powder by thermal evaporation under vacuum of 1.33 × 10^-4 Pa （ 10^-6 Torr） on unheated glass substrates. The effect of thickness on the structural, morphological and optical properties of SnSb2S4 thin films was investigated. Films thickness measured by interference fringes method varied from 50 to 700 nm. X-ray diffraction analysis revealed that all the SnSb2S4 films were polycrystalline in spite without heating the substrates and the crystallinity was improved with increasing film thickness. The microstructure parameters： crystallite size, strain and dislocation density were calculated. It was observed that the crystallite size increased and the crystal defects decreased with increasing film thickness. In addition, by increasing the film thickness, an enhancement in the surface roughness root-mean-square （RMS） increased from 2.0 to 6.6 nm. The fundamental optical parameters like band gap, absorption and extinction coefficient were calculated in the strong absorption region of transmittance and reflectance spectrum. The optical absorption measurements indicated that the band （Eg） gap of the thin films decreased from 2.10 to 1.65 eV with increasing film thickness. The refractive indexes were evaluated in transparent region in terms of envelope method, which was suggested by Swanepoul. It was observed that the refractive index increased with increasing film thickness.
文摘利用溶胶-凝胶法在La Ni O3/Si O2/Si衬底上制备了掺Mn量为0%、1%、5%、10%（质量分数）的0.7Bi Fe O3-0.3Pb Ti O3（BFMPT7030/x,x=0,0.01,0.05,0.1）薄膜。XRD测试表明,薄膜均完全结晶,呈现高度（100）择优取向。通过对薄膜晶体结构分析,发现BFMPT7030/0.05薄膜具有最小的晶粒尺寸（258 nm）及最小的晶胞体积（61.25×10-3 nm3）。SEM测试结果显示样品晶粒生长充分,晶粒尺寸在150~300 nm之间。铁电性能测试结果表明,当Mn含量为5%时,铁电性能较好,电滞回线形状最好,最为饱和。漏电流测试结果表明随着掺Mn量增加,BFMPT7030薄膜的漏电流随电场增大而增加的趋势减弱。