A novel Ni_(30)Cr_(25)Al_(15)Co_(15)Mo_(5)Ti_(5)Y_(5) high-entropy alloy(HEA)coating was irradiated to optimize its internal structure via laser after supersonic particle deposition(SPD).Owing to the high energy densi...A novel Ni_(30)Cr_(25)Al_(15)Co_(15)Mo_(5)Ti_(5)Y_(5) high-entropy alloy(HEA)coating was irradiated to optimize its internal structure via laser after supersonic particle deposition(SPD).Owing to the high energy density of the laser and large temperature gradient,the crystallization process of the molecules and atoms in the coating was restrained and supercooling occurred.Experimental results showed that a considerable number of nano-crystal grains precipitated and amorphous structures were formed because of the random orientation of the crystals.The baseline of differential scanning calorimetry scans obtained for the coating started to shift at the Tg of 939.37℃ and a step was observed.Multiple dispersion peaks and lattice fringes indicated that the nucleation of the irradiated laser-induced topology optimized(LTO)coating was incomplete.The laser-induced topology optimizing treatment led to quasi-isotropy in the SPD coating.Furthermore,the LTO coating exhibited a residual stress of 18.4 MPa,stress-strain response,and fatigue limit of 265 MPa.Hence,the LTO coating exhibited higher performance than the unirradiated SPD coating.The Nyquist and Bode electrochemical impedance spectra of the LTO coating,including two relaxation processes,indicated that the corrosion process steadily recovered to the equilibrium state.This implies that the uniform oxidation passivation layer on the surface of the LTO coating insulated the material from the corrosive medium,protecting the substrate from further corrosion,thus enhancing the structural security of the material for use in super-intense laser facility applications.展开更多
Nanocrystalline molybdenum carbide (Mo2C) was prepared via one simple route by the reaction of metallic magnesium powders with molybdenum trioxide and potassium acetate in an autoclave at the condition of 600℃ and 4 ...Nanocrystalline molybdenum carbide (Mo2C) was prepared via one simple route by the reaction of metallic magnesium powders with molybdenum trioxide and potassium acetate in an autoclave at the condition of 600℃ and 4 h. X-ray powder diffraction (XRD) pattern indicated that the product was hexagonal α-Mo2C, and the cell constant was a = 3.0091 ?, c = 4.7368 ?. Scanning electron microscopy (SEM) image showed that the sample consisted of particles with an average size of about 100 nm in diameter. The product was also studied by the thermogravimetric analysis (TGA). It had good thermal stability and oxidation resistance below 450℃ in air.展开更多
基金supported by a grant from the Natural Science Foundation of Jiangsu Province (Grant No.BK20191036)the Foundation of Research Project of China (Grant No.JCKY 61420051911)。
文摘A novel Ni_(30)Cr_(25)Al_(15)Co_(15)Mo_(5)Ti_(5)Y_(5) high-entropy alloy(HEA)coating was irradiated to optimize its internal structure via laser after supersonic particle deposition(SPD).Owing to the high energy density of the laser and large temperature gradient,the crystallization process of the molecules and atoms in the coating was restrained and supercooling occurred.Experimental results showed that a considerable number of nano-crystal grains precipitated and amorphous structures were formed because of the random orientation of the crystals.The baseline of differential scanning calorimetry scans obtained for the coating started to shift at the Tg of 939.37℃ and a step was observed.Multiple dispersion peaks and lattice fringes indicated that the nucleation of the irradiated laser-induced topology optimized(LTO)coating was incomplete.The laser-induced topology optimizing treatment led to quasi-isotropy in the SPD coating.Furthermore,the LTO coating exhibited a residual stress of 18.4 MPa,stress-strain response,and fatigue limit of 265 MPa.Hence,the LTO coating exhibited higher performance than the unirradiated SPD coating.The Nyquist and Bode electrochemical impedance spectra of the LTO coating,including two relaxation processes,indicated that the corrosion process steadily recovered to the equilibrium state.This implies that the uniform oxidation passivation layer on the surface of the LTO coating insulated the material from the corrosive medium,protecting the substrate from further corrosion,thus enhancing the structural security of the material for use in super-intense laser facility applications.
文摘Nanocrystalline molybdenum carbide (Mo2C) was prepared via one simple route by the reaction of metallic magnesium powders with molybdenum trioxide and potassium acetate in an autoclave at the condition of 600℃ and 4 h. X-ray powder diffraction (XRD) pattern indicated that the product was hexagonal α-Mo2C, and the cell constant was a = 3.0091 ?, c = 4.7368 ?. Scanning electron microscopy (SEM) image showed that the sample consisted of particles with an average size of about 100 nm in diameter. The product was also studied by the thermogravimetric analysis (TGA). It had good thermal stability and oxidation resistance below 450℃ in air.