Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of ...Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.展开更多
The continuous cooling transformation (CCT) diagrams of 86CrMoV7 steel samples including hot deformed and not hot deformed were constructed by dilatometry, metallography and transmission electron microscopy (TEM). The...The continuous cooling transformation (CCT) diagrams of 86CrMoV7 steel samples including hot deformed and not hot deformed were constructed by dilatometry, metallography and transmission electron microscopy (TEM). The results showed that hot deformation accelerated pearlite transformation and fine pearlite microstructure. Moreover, the undissolved carbides became the nucleating sites of pearlite, accelerated pearlite formation and fine pearlite if the steel had been deformed at high temperature. In contrast, undissolved carbides did not make any influence on pearlite transformation if the steel had not been deformed at high temperature.展开更多
基金The present work was financially supported by a China National‘973’Project No.G1998061511the Natural Science Fund of Hebei Province No.501205.
文摘Acicular ferrite microstructure was achieved for an ultralow carbon pipeline steel through the improved thermome chanical control process (TMCP), which was based on the transformation process of deformed austenite of steel. Compared with commercial pipeline steels, the experimental ultralow carbon pipeline steel possessed the satisfied strength and toughness behaviors under the current improved TMCP, although it contained only approximately 0.025% C, vvhich should mainly be attributed to the microstructural characteristics of acicular ferrite.
文摘The continuous cooling transformation (CCT) diagrams of 86CrMoV7 steel samples including hot deformed and not hot deformed were constructed by dilatometry, metallography and transmission electron microscopy (TEM). The results showed that hot deformation accelerated pearlite transformation and fine pearlite microstructure. Moreover, the undissolved carbides became the nucleating sites of pearlite, accelerated pearlite formation and fine pearlite if the steel had been deformed at high temperature. In contrast, undissolved carbides did not make any influence on pearlite transformation if the steel had not been deformed at high temperature.