In this work, the morphologies of weld of 7075-T6 aluminum alloy via friction stir welding （FSW） were analyzed by optical microscopy, the temperature field was attained by numerical simulation, and the effect of tem...In this work, the morphologies of weld of 7075-T6 aluminum alloy via friction stir welding （FSW） were analyzed by optical microscopy, the temperature field was attained by numerical simulation, and the effect of temperature on material transfer behavior in the thermal-mechanical affected zone （TMAZ） at different stages was mainly investigated. The FSW process consists of three stages. It is very interesting to find that the maximum transfer displacement of material appears at the final stage of welding process, then at the stable stage and at the initial stage, which results from the difference of peak temperatures at different stages. At any stage, the material in TMAZ near the surface of weld transfers downwards, the material in the middle of weld moves upwards and the material near the bottom of weld hardly moves. In any cross section of weld, the largest transfer displacement of material appears in the middle of weld. The increase of rotational velocity and the decrease of welding speed are both beneficial to the transfer displacement of material in the middle of weld.展开更多
基金the National Natural Science Foundation of China (No.51204111)the Education Department Foundation of Liaoning Province (No.L2012047)the State Key Lab of Advanced Welding and Joining in Harbin Institute of Technology (AWJ-M13-07)
文摘In this work, the morphologies of weld of 7075-T6 aluminum alloy via friction stir welding （FSW） were analyzed by optical microscopy, the temperature field was attained by numerical simulation, and the effect of temperature on material transfer behavior in the thermal-mechanical affected zone （TMAZ） at different stages was mainly investigated. The FSW process consists of three stages. It is very interesting to find that the maximum transfer displacement of material appears at the final stage of welding process, then at the stable stage and at the initial stage, which results from the difference of peak temperatures at different stages. At any stage, the material in TMAZ near the surface of weld transfers downwards, the material in the middle of weld moves upwards and the material near the bottom of weld hardly moves. In any cross section of weld, the largest transfer displacement of material appears in the middle of weld. The increase of rotational velocity and the decrease of welding speed are both beneficial to the transfer displacement of material in the middle of weld.