Objective Impact of the presence of bacteria associated with a marine dinoflagellate, Alexandrium tamarense CI01, on the growth and toxin production of the algae in batch culture was investigated. Methods Pronounced c...Objective Impact of the presence of bacteria associated with a marine dinoflagellate, Alexandrium tamarense CI01, on the growth and toxin production of the algae in batch culture was investigated. Methods Pronounced changes in the activities of the algal culture were observed when the culture was treated with different doses of a mixture of penicillin and streptomycin. Results In the presence of antibiotics at the initial concentration of 100 u/mL in culture medium, both algal growth and toxin yield increased markedly. When the concentration of antibiotics was increased to 500 u/mL, the microalgal growth was inhibited, but resumed in a few days to eventually reach the same level of growth and toxin production as at the lower dose of the antibiotics. When the antibiotics were present at a concentration of 1 000 u/mL, the algal growth was inhibited permanently. Conclusions The results indicate that antibiotics can enhance algal growth and toxin production not only through their inhibition of the growth and hence competition for nutrients, but also through their effects on the physiology of the algae.展开更多
Conventional MgO-C bricks(graphite content>14 wt.%)produce a great deal of greenhouse gas emission,while low-carbon MgO-C bricks have serious thermal shock resistance during high-temperature service.To enhance the ...Conventional MgO-C bricks(graphite content>14 wt.%)produce a great deal of greenhouse gas emission,while low-carbon MgO-C bricks have serious thermal shock resistance during high-temperature service.To enhance the high-temperature mechanical property and thermal shock resistance of low-carbon MgO-C bricks,a novel route of introducing ZrSiO_(4) powder into low-carbon MgO-C bricks was reported in such refractories with 2 wt.% flaky graphite.The results indicate that the low-carbon MgO-C brick with 0.5 wt.%ZrSiO_(4) addition has the maximum hot modulus of rupture at 1400℃ and the corresponding specimen fired in the carbon embedded atmosphere has the maximum residual strength ratio(98.6%)after three thermal shock cycles.It is found that some needle-like AlON and plate-like Al_(2)O_(3)-ZrO_(2) composites were in situ formed in the matrices after the low-carbon MgO-C bricks were coked at 1400℃,which can enhance the high-temperature mechanical property and thermal shock resistance due to the effect of fiber toughening and particle toughening.Moreover,CO_(2) emission of the newly developed low-carbon MgO-C bricks is reduced by 58.3% per ton steel after using them as the working lining of a 90 t vacuum oxygen decarburization ladle.展开更多
基金This study was supported by the key project of the National 10th Five-Year Plan Programthe research project title was research and development of red tide microalgal toxin (2001BA707B03)
文摘Objective Impact of the presence of bacteria associated with a marine dinoflagellate, Alexandrium tamarense CI01, on the growth and toxin production of the algae in batch culture was investigated. Methods Pronounced changes in the activities of the algal culture were observed when the culture was treated with different doses of a mixture of penicillin and streptomycin. Results In the presence of antibiotics at the initial concentration of 100 u/mL in culture medium, both algal growth and toxin yield increased markedly. When the concentration of antibiotics was increased to 500 u/mL, the microalgal growth was inhibited, but resumed in a few days to eventually reach the same level of growth and toxin production as at the lower dose of the antibiotics. When the antibiotics were present at a concentration of 1 000 u/mL, the algal growth was inhibited permanently. Conclusions The results indicate that antibiotics can enhance algal growth and toxin production not only through their inhibition of the growth and hence competition for nutrients, but also through their effects on the physiology of the algae.
基金Enterprise Research and Development Project of Beijing Lirr High-Temperature Materials Co.,Ltd.(2020-02)Key Scientific Research Project for Universities and Colleges in Henan Province(19A430028)+1 种基金the Excellent Youth Research Project of Anhui Province(2022AH030135)the PhD Research Funding of Suzhou University(2021BSK041).
文摘Conventional MgO-C bricks(graphite content>14 wt.%)produce a great deal of greenhouse gas emission,while low-carbon MgO-C bricks have serious thermal shock resistance during high-temperature service.To enhance the high-temperature mechanical property and thermal shock resistance of low-carbon MgO-C bricks,a novel route of introducing ZrSiO_(4) powder into low-carbon MgO-C bricks was reported in such refractories with 2 wt.% flaky graphite.The results indicate that the low-carbon MgO-C brick with 0.5 wt.%ZrSiO_(4) addition has the maximum hot modulus of rupture at 1400℃ and the corresponding specimen fired in the carbon embedded atmosphere has the maximum residual strength ratio(98.6%)after three thermal shock cycles.It is found that some needle-like AlON and plate-like Al_(2)O_(3)-ZrO_(2) composites were in situ formed in the matrices after the low-carbon MgO-C bricks were coked at 1400℃,which can enhance the high-temperature mechanical property and thermal shock resistance due to the effect of fiber toughening and particle toughening.Moreover,CO_(2) emission of the newly developed low-carbon MgO-C bricks is reduced by 58.3% per ton steel after using them as the working lining of a 90 t vacuum oxygen decarburization ladle.