The vanadium oxide/reduced graphene oxide（V2 O5/rGO） composite catalyst which determined the selective catalytic reduction activity（SCR） of NO with NH3 was prepared by a simple solvothermal method. The physicochem...The vanadium oxide/reduced graphene oxide（V2 O5/rGO） composite catalyst which determined the selective catalytic reduction activity（SCR） of NO with NH3 was prepared by a simple solvothermal method. The physicochemical properties of the catalysts were characterized by X-ray diffraction（XRD）, scanning electron microscopy（SEM）, Raman, X-ray energy spectrometer（XPS） and N2 sorption isotherm measurement（BET）. Results of NH3-SCR showed that the NO conversion of V2 O5/rGO catalyst could reach 54.3% at 100 ℃. And the removal of NO increased to 74.6% when the temperature was up to 220 ℃. By characterizing the microstructure and morphology of the V2 O5/rGO catalysts prepared by in-situ growth and mechanical mixing methods, it was further shown that V2 O5 nanoparticles were highly dispersed and in situ growth on the rGO surface. Based on X-ray energy spectrometer, V2 O5/r GO catalyst had good low temperature denitrification performance due to the chemical adsorption oxygen and low-valent vanadium oxide contained in V2 O5/rGO catalyst, which was beneficial to the redox reaction between V2 O5 and graphene.展开更多
基金Funded by the National Natural Science Foundation of China(No.51506155)Wuhan Science and Technology Project(No.2016010101010020)
文摘The vanadium oxide/reduced graphene oxide（V2 O5/rGO） composite catalyst which determined the selective catalytic reduction activity（SCR） of NO with NH3 was prepared by a simple solvothermal method. The physicochemical properties of the catalysts were characterized by X-ray diffraction（XRD）, scanning electron microscopy（SEM）, Raman, X-ray energy spectrometer（XPS） and N2 sorption isotherm measurement（BET）. Results of NH3-SCR showed that the NO conversion of V2 O5/rGO catalyst could reach 54.3% at 100 ℃. And the removal of NO increased to 74.6% when the temperature was up to 220 ℃. By characterizing the microstructure and morphology of the V2 O5/rGO catalysts prepared by in-situ growth and mechanical mixing methods, it was further shown that V2 O5 nanoparticles were highly dispersed and in situ growth on the rGO surface. Based on X-ray energy spectrometer, V2 O5/r GO catalyst had good low temperature denitrification performance due to the chemical adsorption oxygen and low-valent vanadium oxide contained in V2 O5/rGO catalyst, which was beneficial to the redox reaction between V2 O5 and graphene.