Zr was added to Ti−Nb−Fe alloys to develop low elastic modulus and high strengthβ-Ti alloys for biomedical applications.Ingots of Ti−12Nb−2Fe−(2,4,6,8,10)Zr(at.%)were prepared by arc melting and then subjected to hom...Zr was added to Ti−Nb−Fe alloys to develop low elastic modulus and high strengthβ-Ti alloys for biomedical applications.Ingots of Ti−12Nb−2Fe−(2,4,6,8,10)Zr(at.%)were prepared by arc melting and then subjected to homogenization,cold rolling,and solution treatments.The phases and microstructures of the alloys were analyzed by optical microscopy,X-ray diffraction,and transmission electron microscopy.The mechanical properties were measured by tensile tests.The results indicate that Zr and Fe cause a remarkable solid-solution strengthening effect on the alloys;thus,all the alloys show yield and ultimate tensile strengths higher than 510 MPa and 730 MPa,respectively.Zr plays a weak role in the deformation mechanism.Further,twinning occurs in all the deformed alloys and is beneficial to both strength and plasticity.Ti−12Nb−2Fe−(8,10)Zr alloys with metastableβphases show low elastic modulus,high tensile strength,and good plasticity and are suitable candidate materials for biomedical implants.展开更多
Although Electron Beam Melting (EBM) is an innovative technology, the fatigue properties of materials manufactured by EBM may be lower than those of casted and wrought materials due to defects and surface roughness. I...Although Electron Beam Melting (EBM) is an innovative technology, the fatigue properties of materials manufactured by EBM may be lower than those of casted and wrought materials due to defects and surface roughness. In order to enhance the fatigue life of components or structures manufactured by EBM, a mechanical surface treatment technology, e.g., peening, would be effective because peening introduces high compressive residual stress at the surface which can extend the fatigue life considerably. In the present study, specimens were manufactured by EBM using titanium alloy Ti-6Al-4V powder. Two types of specimens were prepared: as-built and as-machined specimens. Specimens of each type were treated by cavitation peening or shot peening. The fatigue lives of the specimens were evaluated by a plate bending fatigue tester. The residual stress and surface roughness were also evaluated. The results obtained showed that the fatigue strength of as-built specimens can be improved by 21% by cavitation peening or shot peening, and the fatigue life under particular applied stresses can also be extended by 178% by cavitation peening.展开更多
基金the Natural Science Foundation of Shanghai,China(No.15ZR1428400)Shanghai Engineering Research Center of High-Performance Medical Device Materials,China(No.20DZ2255500)the Project of Creation of Life Innovation Materials for Interdisciplinary and International Researcher Development,Tohoku University,sponsored by Ministry,Education,Culture,Sports,Science and Technology,Japan,and the Grant-in Aid for Scientific Research(C)(No.20K05139)from JSPS(Japan Society for the Promotion of Science),Tokyo,Japan.
文摘Zr was added to Ti−Nb−Fe alloys to develop low elastic modulus and high strengthβ-Ti alloys for biomedical applications.Ingots of Ti−12Nb−2Fe−(2,4,6,8,10)Zr(at.%)were prepared by arc melting and then subjected to homogenization,cold rolling,and solution treatments.The phases and microstructures of the alloys were analyzed by optical microscopy,X-ray diffraction,and transmission electron microscopy.The mechanical properties were measured by tensile tests.The results indicate that Zr and Fe cause a remarkable solid-solution strengthening effect on the alloys;thus,all the alloys show yield and ultimate tensile strengths higher than 510 MPa and 730 MPa,respectively.Zr plays a weak role in the deformation mechanism.Further,twinning occurs in all the deformed alloys and is beneficial to both strength and plasticity.Ti−12Nb−2Fe−(8,10)Zr alloys with metastableβphases show low elastic modulus,high tensile strength,and good plasticity and are suitable candidate materials for biomedical implants.
文摘Although Electron Beam Melting (EBM) is an innovative technology, the fatigue properties of materials manufactured by EBM may be lower than those of casted and wrought materials due to defects and surface roughness. In order to enhance the fatigue life of components or structures manufactured by EBM, a mechanical surface treatment technology, e.g., peening, would be effective because peening introduces high compressive residual stress at the surface which can extend the fatigue life considerably. In the present study, specimens were manufactured by EBM using titanium alloy Ti-6Al-4V powder. Two types of specimens were prepared: as-built and as-machined specimens. Specimens of each type were treated by cavitation peening or shot peening. The fatigue lives of the specimens were evaluated by a plate bending fatigue tester. The residual stress and surface roughness were also evaluated. The results obtained showed that the fatigue strength of as-built specimens can be improved by 21% by cavitation peening or shot peening, and the fatigue life under particular applied stresses can also be extended by 178% by cavitation peening.