The effect of Fe-impurity（0.2%-2%, mass fraction） on the microstructure, dry sliding wear, and friction properties of Al-15 Mg2 Si composite was investigated using a pin-on-disk tester under the applied pressures of...The effect of Fe-impurity（0.2%-2%, mass fraction） on the microstructure, dry sliding wear, and friction properties of Al-15 Mg2 Si composite was investigated using a pin-on-disk tester under the applied pressures of 0.25, 0.5 and 1 MPa at a constant sliding speed of 0.13 m/s. According to the results, Fe modified the primary Mg2 Si particles from irregular dendritic form to smaller particles with polyhedral shapes, refined the pseudo-eutectic structure, and led to the formation of hard b-Al5 Fe Si platelets in the matrix. In spite of hardness improvement by these microstructural changes, the resistance of the composite against dry sliding wear was impaired. SEM examination of the worn surfaces, wear debris, and subsurface regions confirmed the negative effect of b-phase on the tribological properties. It was found that b-particles were fractured easily, thereby decreasing the potential of the substrate to resist against sliding stresses and giving rise to the instability and easy detachment of tribolayer as large delaminated debris. The friction results also revealed that Fe slightly decreased the average friction coefficient, but increased the fluctuation in friction.展开更多
The effects of Cu addition（0.5%, 1%, 1.5%, 2%, and 3%, mass fraction） on the quality index（Qi） and hot tearing susceptibility（HTS） of A356 alloy were investigated. According to the results, Cu addition up to 1.5...The effects of Cu addition（0.5%, 1%, 1.5%, 2%, and 3%, mass fraction） on the quality index（Qi） and hot tearing susceptibility（HTS） of A356 alloy were investigated. According to the results, Cu addition up to 1.5% increases the Qi by almost 10%, which seems to be due to its solid solution strengthening and dispersion hardening effect of Cu-rich Al2Cu and AlMgCuSi compounds. However, further addition of Cu（up to 3%） decreases the Qi by almost 12%, which is likely due to the reduction of tensile strength and elongation caused by increased volume fraction of brittle Cu-rich intermetallics and microporosities in the microstructure. It is also found that Cu increases the HTS of A356 alloy measured by constrained rod casting method. According to the thermal analysis results, Cu widens the solidification range of the alloy, which in turn, decreases its fluidity and increases the time period during which the mushy-state alloy is exposed to the hot tearing susceptible zone. SEM examination of the hot tear surfaces in high-Cu alloys also demonstrates their rough nature and the occurrence of interdendritic/intergranular microcracks as convincing evidences for the initiation of hot tears in the late stages of solidification in which there is not enough time for crack healing.展开更多
The effect of different cooling rates(2.7,5.5,17.1,and 57.5℃/s)on the solidification parameters,microstructure,and mechanical properties of Al-15Mg_(2)Si composites was studied.The results showed that a high cooling ...The effect of different cooling rates(2.7,5.5,17.1,and 57.5℃/s)on the solidification parameters,microstructure,and mechanical properties of Al-15Mg_(2)Si composites was studied.The results showed that a high cooling rate refined the Mg_(2)Si particles and changed their morphology to more compacted forms with less microcracking tendency.The average radius and fraction of primary Mg_(2)Si particles decreased from 20μm and 13.5%to about 10μm and 7.3%,respectively,as the cooling rate increased from 2.7 to 57.5℃/s.Increasing the cooling rate also improved the distribution of microconstituents and decreased the grain size and volume fraction of micropores.The mechanical properties results revealed that augmenting the cooling rate from 2.7 to about 57.5℃/s increased the hardness and quality index by 25%and245%,respectively.The high cooling rate also changed the fracture mechanism from a brittle-dominated mode to a high-energy ductile mode comprising extensive dimpled zones.展开更多
Two theoretical criteria represented by Katgerman, and Clyne and Davies for prognosticating hot tearing sensitivity were compared. Both unrefined and grain-refined samples of Al2024 alloy were solidified at various co...Two theoretical criteria represented by Katgerman, and Clyne and Davies for prognosticating hot tearing sensitivity were compared. Both unrefined and grain-refined samples of Al2024 alloy were solidified at various cooling rates ranging from 0.4 to 17.5 °C/s. Thermal analysis was used to detect dendrite coherency point and temperature of eutectic reaction. Curves of solid and liquid fractions were plotted based on Newtonian method to determine hot tearing susceptible areas. The experimental results show that the most susceptible zone in which hot tearing can occur in Al2024 is where Al_2CuMg intermetallic compound forms as a eutectic phase at last stage of mushy-state interval. Also, both criteria are in a good agreement with each other at high cooling rates used in direct-chill casting process while Clyne and Davies＇ model is more acceptable to determine hot tearing tendency from low to medium cooling rates.展开更多
文摘The effect of Fe-impurity（0.2%-2%, mass fraction） on the microstructure, dry sliding wear, and friction properties of Al-15 Mg2 Si composite was investigated using a pin-on-disk tester under the applied pressures of 0.25, 0.5 and 1 MPa at a constant sliding speed of 0.13 m/s. According to the results, Fe modified the primary Mg2 Si particles from irregular dendritic form to smaller particles with polyhedral shapes, refined the pseudo-eutectic structure, and led to the formation of hard b-Al5 Fe Si platelets in the matrix. In spite of hardness improvement by these microstructural changes, the resistance of the composite against dry sliding wear was impaired. SEM examination of the worn surfaces, wear debris, and subsurface regions confirmed the negative effect of b-phase on the tribological properties. It was found that b-particles were fractured easily, thereby decreasing the potential of the substrate to resist against sliding stresses and giving rise to the instability and easy detachment of tribolayer as large delaminated debris. The friction results also revealed that Fe slightly decreased the average friction coefficient, but increased the fluctuation in friction.
文摘The effects of Cu addition（0.5%, 1%, 1.5%, 2%, and 3%, mass fraction） on the quality index（Qi） and hot tearing susceptibility（HTS） of A356 alloy were investigated. According to the results, Cu addition up to 1.5% increases the Qi by almost 10%, which seems to be due to its solid solution strengthening and dispersion hardening effect of Cu-rich Al2Cu and AlMgCuSi compounds. However, further addition of Cu（up to 3%） decreases the Qi by almost 12%, which is likely due to the reduction of tensile strength and elongation caused by increased volume fraction of brittle Cu-rich intermetallics and microporosities in the microstructure. It is also found that Cu increases the HTS of A356 alloy measured by constrained rod casting method. According to the thermal analysis results, Cu widens the solidification range of the alloy, which in turn, decreases its fluidity and increases the time period during which the mushy-state alloy is exposed to the hot tearing susceptible zone. SEM examination of the hot tear surfaces in high-Cu alloys also demonstrates their rough nature and the occurrence of interdendritic/intergranular microcracks as convincing evidences for the initiation of hot tears in the late stages of solidification in which there is not enough time for crack healing.
文摘The effect of different cooling rates(2.7,5.5,17.1,and 57.5℃/s)on the solidification parameters,microstructure,and mechanical properties of Al-15Mg_(2)Si composites was studied.The results showed that a high cooling rate refined the Mg_(2)Si particles and changed their morphology to more compacted forms with less microcracking tendency.The average radius and fraction of primary Mg_(2)Si particles decreased from 20μm and 13.5%to about 10μm and 7.3%,respectively,as the cooling rate increased from 2.7 to 57.5℃/s.Increasing the cooling rate also improved the distribution of microconstituents and decreased the grain size and volume fraction of micropores.The mechanical properties results revealed that augmenting the cooling rate from 2.7 to about 57.5℃/s increased the hardness and quality index by 25%and245%,respectively.The high cooling rate also changed the fracture mechanism from a brittle-dominated mode to a high-energy ductile mode comprising extensive dimpled zones.
文摘Two theoretical criteria represented by Katgerman, and Clyne and Davies for prognosticating hot tearing sensitivity were compared. Both unrefined and grain-refined samples of Al2024 alloy were solidified at various cooling rates ranging from 0.4 to 17.5 °C/s. Thermal analysis was used to detect dendrite coherency point and temperature of eutectic reaction. Curves of solid and liquid fractions were plotted based on Newtonian method to determine hot tearing susceptible areas. The experimental results show that the most susceptible zone in which hot tearing can occur in Al2024 is where Al_2CuMg intermetallic compound forms as a eutectic phase at last stage of mushy-state interval. Also, both criteria are in a good agreement with each other at high cooling rates used in direct-chill casting process while Clyne and Davies＇ model is more acceptable to determine hot tearing tendency from low to medium cooling rates.