With the vigorous development of China’s iron and steel industry and the introduction of ultra-low emission policies, the emission of pollutants such as SO2 and NOx has received unprecedented attention. At present, t...With the vigorous development of China’s iron and steel industry and the introduction of ultra-low emission policies, the emission of pollutants such as SO2 and NOx has received unprecedented attention. At present, the commonly used denitrification methods include selective catalytic reduction (SCR), active coke, etc. As a newly developed denitrification technology, oxidation denitrification is not widely used, and the technical level is mixed, and there might be problems such as yellow smoke, secondary pollution and ozone escape in the practical application. In this paper, problems existing in the denitrification process of sintering flue gas oxidation are analyzed, and a 320 m2 sintering machine is taken as an example. Comparing the denitrification technology of sintering industry, it could be seen that the denitrification technology route of oxidation method has low pollution, low cost and high comprehensive environmental benefits, and has greatly potential development.展开更多
The surface treatment technology of hot aluminum-zinc steel plate and UV curing technology may be effectively combined in the present research. According to different light curing mechanisms, different formulations fr...The surface treatment technology of hot aluminum-zinc steel plate and UV curing technology may be effectively combined in the present research. According to different light curing mechanisms, different formulations from UV curing surface treatment agents can be applied to the surface treatment of hot aluminum-zinc steel plate, mainly including 3-ethyl-3-benzoxy-methyl oxacyclobutane (TCM 104) and 3,4-epoxy-cyclohexylformic acid -3',4'-epoxy-cyclohexyl methyl ester (UVR 6110) as active diluents, high molecular weight polyfunctional oxacyclobutane as oligomer, triaryl sulfonium salt as a cationic photoinitiator, and an anthracene compound as a sensitizer. 385 nm LED lamp used as a radiation resource, the effects of the proportion of active diluent, the type and amount of photoinitiator, the amount of sensitizer, the curing temperature, and the amount of nano-SiO<sub>2</sub> on the photocuring rate were investigated by photoper-scanning differential calorimetry (Photo-DSC). The experimental results show that the system has the fastest photocuring rate under the conditions of 8:2 ratio of TCM 104 to UVR 6110, 2.5% photoinitiator, 0.6% sensitizer, 0.2% nano-SiO<sub>2</sub> additive, and 80˚C curing temperature. Based on addition of the appropriate number of various additives, the cationic photocuring surface treatment solution was prepared and further coated on the hot-dip galvalume steel plates. After curing, the passivation films were characterized by neutral salt spray test (NSST), Fourier transform infrared spectroscopy (FT-IR), electrochemical testing and other methods. The results show that the formulations could be cured at an energy of 150 mJ/cm<sup>2</sup>, and the overall performance of the passivation film could meet with the requirements of the downstream users.展开更多
文摘With the vigorous development of China’s iron and steel industry and the introduction of ultra-low emission policies, the emission of pollutants such as SO2 and NOx has received unprecedented attention. At present, the commonly used denitrification methods include selective catalytic reduction (SCR), active coke, etc. As a newly developed denitrification technology, oxidation denitrification is not widely used, and the technical level is mixed, and there might be problems such as yellow smoke, secondary pollution and ozone escape in the practical application. In this paper, problems existing in the denitrification process of sintering flue gas oxidation are analyzed, and a 320 m2 sintering machine is taken as an example. Comparing the denitrification technology of sintering industry, it could be seen that the denitrification technology route of oxidation method has low pollution, low cost and high comprehensive environmental benefits, and has greatly potential development.
文摘The surface treatment technology of hot aluminum-zinc steel plate and UV curing technology may be effectively combined in the present research. According to different light curing mechanisms, different formulations from UV curing surface treatment agents can be applied to the surface treatment of hot aluminum-zinc steel plate, mainly including 3-ethyl-3-benzoxy-methyl oxacyclobutane (TCM 104) and 3,4-epoxy-cyclohexylformic acid -3',4'-epoxy-cyclohexyl methyl ester (UVR 6110) as active diluents, high molecular weight polyfunctional oxacyclobutane as oligomer, triaryl sulfonium salt as a cationic photoinitiator, and an anthracene compound as a sensitizer. 385 nm LED lamp used as a radiation resource, the effects of the proportion of active diluent, the type and amount of photoinitiator, the amount of sensitizer, the curing temperature, and the amount of nano-SiO<sub>2</sub> on the photocuring rate were investigated by photoper-scanning differential calorimetry (Photo-DSC). The experimental results show that the system has the fastest photocuring rate under the conditions of 8:2 ratio of TCM 104 to UVR 6110, 2.5% photoinitiator, 0.6% sensitizer, 0.2% nano-SiO<sub>2</sub> additive, and 80˚C curing temperature. Based on addition of the appropriate number of various additives, the cationic photocuring surface treatment solution was prepared and further coated on the hot-dip galvalume steel plates. After curing, the passivation films were characterized by neutral salt spray test (NSST), Fourier transform infrared spectroscopy (FT-IR), electrochemical testing and other methods. The results show that the formulations could be cured at an energy of 150 mJ/cm<sup>2</sup>, and the overall performance of the passivation film could meet with the requirements of the downstream users.