The normalization method has been employed to estimate the J-resistance (J—R) curves for C-shaped outside edge-notched compression (COEC) specimens of SA-508 steel. The COEC specimens present the lowest J—R curves i...The normalization method has been employed to estimate the J-resistance (J—R) curves for C-shaped outside edge-notched compression (COEC) specimens of SA-508 steel. The COEC specimens present the lowest J—R curves in comparison with other three types of specimens. Based on the J—Q—M met hod, the constraint parame ter Q determined at the mid-plane in the through-thickness direction of the specimen is used to approximately quantify the threedimensional crack-tip constraint for COEC specimens. Combining with the previous experiments on J—R curves, the constraint-coirected J—R curves for SA-508 steel specimens are given, which may be used to predict the fracture toughness of actual cracked components in structural integrity assessment.展开更多
Based on the test results obtained from the single-step test and the incremental-step test at room temperature and 240℃, a probabilistic assessment of temperature effects on the cyclic stress-strum response and the f...Based on the test results obtained from the single-step test and the incremental-step test at room temperature and 240℃, a probabilistic assessment of temperature effects on the cyclic stress-strum response and the fatigue life of 1Cr18Ni9Ti steel weld metal is performed. In orber to assess the temperature effect on cyclic stress amplitude where there is a scatter of the material cyclic constitution, a probabilistic assessment approach on the basis of probabilistic modified Ramberg-Osgood relations is introduced.The investigation shows that the cyclic stress amplitude and the scatter of cyclic stress amplitude data are decreased at 240℃. Similarly, from the consideration of the fatigue life scatter a probabilistic assessment of temperature effect on the fatigue life is suggested on the basis of probabilistic Langer S-N relations. The investigation shows that the crack initiation life is increased and the scatter of crack initiation life data is decreased at 240℃.展开更多
基金the National Natural Science Foundation of China (Grant No. 11872320).
文摘The normalization method has been employed to estimate the J-resistance (J—R) curves for C-shaped outside edge-notched compression (COEC) specimens of SA-508 steel. The COEC specimens present the lowest J—R curves in comparison with other three types of specimens. Based on the J—Q—M met hod, the constraint parame ter Q determined at the mid-plane in the through-thickness direction of the specimen is used to approximately quantify the threedimensional crack-tip constraint for COEC specimens. Combining with the previous experiments on J—R curves, the constraint-coirected J—R curves for SA-508 steel specimens are given, which may be used to predict the fracture toughness of actual cracked components in structural integrity assessment.
文摘Based on the test results obtained from the single-step test and the incremental-step test at room temperature and 240℃, a probabilistic assessment of temperature effects on the cyclic stress-strum response and the fatigue life of 1Cr18Ni9Ti steel weld metal is performed. In orber to assess the temperature effect on cyclic stress amplitude where there is a scatter of the material cyclic constitution, a probabilistic assessment approach on the basis of probabilistic modified Ramberg-Osgood relations is introduced.The investigation shows that the cyclic stress amplitude and the scatter of cyclic stress amplitude data are decreased at 240℃. Similarly, from the consideration of the fatigue life scatter a probabilistic assessment of temperature effect on the fatigue life is suggested on the basis of probabilistic Langer S-N relations. The investigation shows that the crack initiation life is increased and the scatter of crack initiation life data is decreased at 240℃.