Alloys with composition of Mg_(96-x)Gd_3Zn_1Li_x(at.%)(x=0, 2, 4, and 6) were prepared by conventional casting. The microstructures of these alloys under as-cast and solid-solution conditions have been observed, and t...Alloys with composition of Mg_(96-x)Gd_3Zn_1Li_x(at.%)(x=0, 2, 4, and 6) were prepared by conventional casting. The microstructures of these alloys under as-cast and solid-solution conditions have been observed, and the mechanical properties were investigated. The results showed that Li is an effective element to refine the grains and break the eutectic networks in as-cast MgGd_3Zn_1 alloy. During solid solution treatment, these broken eutectic networks are spheroidized and highly dispersed. In addition, plentiful lamellar long period stacking ordered(LPSO) phases are precipitated in an α-Mg matrix when the Li addition is not more than 4%. Solid-solution treated Mg_(92)Gd_3Zn_1Li_4 alloy exhibits an optimal ultimate tensile strength(UTS) of 226 MPa and elongation of 5.8%. The strength of MgGd_3Zn_1 alloy is improved significantly, meanwhile, the toughness is apparently increased.展开更多
基金supported by the National Natural Science Foundation of China(Nos.50571073,51574175 and 51474153)the Ph. D. Programs Foundation of Ministry of Education of China(20111402110004)the Natural Science Foundation of Shanxi Province(Nos.2009011028-3 and 2012011022-1)
文摘Alloys with composition of Mg_(96-x)Gd_3Zn_1Li_x(at.%)(x=0, 2, 4, and 6) were prepared by conventional casting. The microstructures of these alloys under as-cast and solid-solution conditions have been observed, and the mechanical properties were investigated. The results showed that Li is an effective element to refine the grains and break the eutectic networks in as-cast MgGd_3Zn_1 alloy. During solid solution treatment, these broken eutectic networks are spheroidized and highly dispersed. In addition, plentiful lamellar long period stacking ordered(LPSO) phases are precipitated in an α-Mg matrix when the Li addition is not more than 4%. Solid-solution treated Mg_(92)Gd_3Zn_1Li_4 alloy exhibits an optimal ultimate tensile strength(UTS) of 226 MPa and elongation of 5.8%. The strength of MgGd_3Zn_1 alloy is improved significantly, meanwhile, the toughness is apparently increased.