Large size,high-density(99.97%)and well-organized Al2O3/Y3Al5O12(YAG)eutectic ceramics were prepared by the modified Bridgman method.The evolution of the three dimensional microstructure and micropores were investigat...Large size,high-density(99.97%)and well-organized Al2O3/Y3Al5O12(YAG)eutectic ceramics were prepared by the modified Bridgman method.The evolution of the three dimensional microstructure and micropores were investigated.The diameter of the micro-pores and the porosity decreased during directional solidification.The average equivalent diam eter of the micro-pores was 2.41μm in the well-prepared eutectic ceramics.Most of the pores(98.07%)were smaller than 4μm.These data are comparable to those prepared by the optical floating zone method.The as-grown eutectic ceramics were polycrystalline,but the interfaces were well-bonded and there were no amorphous phases in the microstructure.The misfits of the different crystallographic relationships were calculated,and the bottleneck of the single-crystal preparation was identified.These results could provide theoretical guidance for the preparation of large,single-crystal Al2O3/YAG eutectic ceramics by the modified Bridgman method.展开更多
基金financially supported by the National Natural Science Foundation of China (Nos. 51804252 and 51701156)the Equipment Pre-Research Foundation of China (Nos. 6140759040102 and 6140923040203)the Doctoral Starting Fund of Xi’an University of Technology (No. 101-451116013)
文摘Large size,high-density(99.97%)and well-organized Al2O3/Y3Al5O12(YAG)eutectic ceramics were prepared by the modified Bridgman method.The evolution of the three dimensional microstructure and micropores were investigated.The diameter of the micro-pores and the porosity decreased during directional solidification.The average equivalent diam eter of the micro-pores was 2.41μm in the well-prepared eutectic ceramics.Most of the pores(98.07%)were smaller than 4μm.These data are comparable to those prepared by the optical floating zone method.The as-grown eutectic ceramics were polycrystalline,but the interfaces were well-bonded and there were no amorphous phases in the microstructure.The misfits of the different crystallographic relationships were calculated,and the bottleneck of the single-crystal preparation was identified.These results could provide theoretical guidance for the preparation of large,single-crystal Al2O3/YAG eutectic ceramics by the modified Bridgman method.