Alluaudite-type NaMnV2(PO4)3 single crystal was successfully synthesized in the NaCl molten-salt media. The single-crystal diffraction data analysis shows that NaMnV2(PO4)3 crystallizes in monoclinic C2/c space group ...Alluaudite-type NaMnV2(PO4)3 single crystal was successfully synthesized in the NaCl molten-salt media. The single-crystal diffraction data analysis shows that NaMnV2(PO4)3 crystallizes in monoclinic C2/c space group with a = 12.098(2), b = 12.415(2), c = 6.4543(11)?, β = 114.614(2)°, V = 881.3(3) ?3, Mr = 464.64, Dc = 3.50158 g/cm3, μ(Mo Kα) = 4.046 mm-1, F(000) = 892.4 and Z = 2. The structure consists of MnO6, VO6 octahedra and PO4 tetrahedra, which form a three-dimensional architecture with two sets of large Na+ tunnels. The intercalation/deintercalation properties of NaMnV2(PO4)3 as positive and negative electrodes were tested in sodium batteries.展开更多
基金supported by the Fund of Education Committee of Shaanxi Province(No.16JS103)the Natural Science Basic Research Plan in Shaanxi Province(No.2018JM2021)
文摘Alluaudite-type NaMnV2(PO4)3 single crystal was successfully synthesized in the NaCl molten-salt media. The single-crystal diffraction data analysis shows that NaMnV2(PO4)3 crystallizes in monoclinic C2/c space group with a = 12.098(2), b = 12.415(2), c = 6.4543(11)?, β = 114.614(2)°, V = 881.3(3) ?3, Mr = 464.64, Dc = 3.50158 g/cm3, μ(Mo Kα) = 4.046 mm-1, F(000) = 892.4 and Z = 2. The structure consists of MnO6, VO6 octahedra and PO4 tetrahedra, which form a three-dimensional architecture with two sets of large Na+ tunnels. The intercalation/deintercalation properties of NaMnV2(PO4)3 as positive and negative electrodes were tested in sodium batteries.