The oxygen adsorption/desorption properties of double perovskite structure oxides PrBaCo2O5＋δ,GdBaCo2O5＋δ,and YBaCo2O5＋δ were investigated by the thermogravimetry（TG）method in the temperature range of 400~900 ...The oxygen adsorption/desorption properties of double perovskite structure oxides PrBaCo2O5＋δ,GdBaCo2O5＋δ,and YBaCo2O5＋δ were investigated by the thermogravimetry（TG）method in the temperature range of 400~900 ℃.The calculated oxygen adsorption/desorption surface reaction rate constants ka and kd of these double perovskite structure oxides were larger than the commonly used cubic perovskite oxides,such as Ba0.95Ca0.05Co0.8Fe0.2O3-δ and Ba0.5Sr0.5Co0.8Fe0.2O3-δ,whereas,the oxygen permeation flux was comparable to that of the latter,which was attributed to the smaller difference of oxygen vacancy in oxygen and nitrogen atmosphere（Δδ/Vmol）in these double perovskite structure oxides.The large oxygen adsorption/desorption rate constants of GdBaCo2O5＋δ and PrBaCo2O5＋δ made them nice catalyst coating materials,on other membrane surfaces,to improve the oxygen permeability.展开更多
基金Project supported by the Natural Science Foundation of Henan Province(0511053400)
文摘The oxygen adsorption/desorption properties of double perovskite structure oxides PrBaCo2O5＋δ,GdBaCo2O5＋δ,and YBaCo2O5＋δ were investigated by the thermogravimetry（TG）method in the temperature range of 400~900 ℃.The calculated oxygen adsorption/desorption surface reaction rate constants ka and kd of these double perovskite structure oxides were larger than the commonly used cubic perovskite oxides,such as Ba0.95Ca0.05Co0.8Fe0.2O3-δ and Ba0.5Sr0.5Co0.8Fe0.2O3-δ,whereas,the oxygen permeation flux was comparable to that of the latter,which was attributed to the smaller difference of oxygen vacancy in oxygen and nitrogen atmosphere（Δδ/Vmol）in these double perovskite structure oxides.The large oxygen adsorption/desorption rate constants of GdBaCo2O5＋δ and PrBaCo2O5＋δ made them nice catalyst coating materials,on other membrane surfaces,to improve the oxygen permeability.