Eu-doped transparent oxyfluoride borosilicate glass ceramics containing Ba2GdF7 nanocrystals were prepared by controlling crys-tallization of melt-quenched glass fabricated under a reductive atmosphere.In the oxyfluor...Eu-doped transparent oxyfluoride borosilicate glass ceramics containing Ba2GdF7 nanocrystals were prepared by controlling crys-tallization of melt-quenched glass fabricated under a reductive atmosphere.In the oxyfluoride borosilicate glass ceramics,the mean crystal size of Ba2GdF7 nanocrystals was about 30 nm,which could be observed by X-ray diffraction（XRD） and transmission electron microscopy analysis.The photoluminescence spectra of the samples excited at 392 nm showed that,besides the characteristic sharp emissions of Eu3＋ ions,a very intense broadband emission of Eu2＋ ions centered at 450 nm appeared.The photoluminescence intensity of Eu3＋ and Eu2＋ ions in the glass ceramics was much stronger than that in the as-made precursor.The long decay lifetimes of Eu3＋ and Eu2＋ ions evidenced the partitions of Eu3＋ and Eu2＋ ions into the Ba2GdF7 nanocrystals.The energy transfer from Gd3＋ ions to Eu3＋ and Eu2＋ ions was confirmed by the excita-tion and emission spectra.展开更多
基金Project supported by the National Science Foundation of China (51072190 and 11004177)Program for New Century Excellent Talents in University (NCET-07-0786)Zhejiang Provincial Natural Science Foundation of China (Z4100030 and Y4110621)
文摘Eu-doped transparent oxyfluoride borosilicate glass ceramics containing Ba2GdF7 nanocrystals were prepared by controlling crys-tallization of melt-quenched glass fabricated under a reductive atmosphere.In the oxyfluoride borosilicate glass ceramics,the mean crystal size of Ba2GdF7 nanocrystals was about 30 nm,which could be observed by X-ray diffraction（XRD） and transmission electron microscopy analysis.The photoluminescence spectra of the samples excited at 392 nm showed that,besides the characteristic sharp emissions of Eu3＋ ions,a very intense broadband emission of Eu2＋ ions centered at 450 nm appeared.The photoluminescence intensity of Eu3＋ and Eu2＋ ions in the glass ceramics was much stronger than that in the as-made precursor.The long decay lifetimes of Eu3＋ and Eu2＋ ions evidenced the partitions of Eu3＋ and Eu2＋ ions into the Ba2GdF7 nanocrystals.The energy transfer from Gd3＋ ions to Eu3＋ and Eu2＋ ions was confirmed by the excita-tion and emission spectra.