The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensil...The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensile test.The mean grain sizes ofα-Mg matrix in the three extruded alloys are 6,8 and 12μm,respectively,slightly increasing with the addition of Y. The relationship between microstructure and strength was discussed in detail.The results show that the addition of Y has little effect on the grain refinement of the as-extruded Mg-Sn based alloys above.The only MgSnY phase is detected in the Mg-Sn-1.5%Y alloy, and the Sn3Y5 phase in the Mg-Sn-3.5%Y alloy,whereas both of them simultaneously exist in the Mg-Sn-3.0%Y alloy.The particle shape of MgSnY and Sn3Y5 phase,inherited from the solidification,has little change before and after hot extrusion.Mg-Sn-3.0%Y alloy has the highest ultimate tensile strength(UTS),305 MPa,by over 50%compared with that of the other two alloys.展开更多
The phase equilibria and compositions in Mg-rich comer at 300℃ were determined in the Mg-Zn-A1 ternary system through the equilibrated alloy method by using X-ray diffraction （XRD） and scanning electron microscopy ...The phase equilibria and compositions in Mg-rich comer at 300℃ were determined in the Mg-Zn-A1 ternary system through the equilibrated alloy method by using X-ray diffraction （XRD） and scanning electron microscopy （SEM） assisted with energy dispersive spectroscopy of X-ray （EDS）. The results show that there exist three three-phase regions consisted of a-Mg＋Mg17A112（7）＋A15Mg11Zn4（φ）, a-Mg＋Mga2（Al, Zn）49（r）＋A15MgllZn4（φ） and a-Mg＋MgZn＋Mg32（A1, Zn）49（r）, respectively. The intermetallic compounds in equilibrium with a-Mg phase all have large composition ranges, not appear to be linear. At the same time, both zinc and aluminum are soluble in the a-Mg solid solution, with which the compounds are in equilibrium.展开更多
基金Project(2008S089)supported by the Key Laboratory Fund of Liaoning Province,ChinaProject(2007010303025)supported by Shenyang Talents Supporting ProgramProject(50731002)supported by the National Natural Science Foundation of China
文摘The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensile test.The mean grain sizes ofα-Mg matrix in the three extruded alloys are 6,8 and 12μm,respectively,slightly increasing with the addition of Y. The relationship between microstructure and strength was discussed in detail.The results show that the addition of Y has little effect on the grain refinement of the as-extruded Mg-Sn based alloys above.The only MgSnY phase is detected in the Mg-Sn-1.5%Y alloy, and the Sn3Y5 phase in the Mg-Sn-3.5%Y alloy,whereas both of them simultaneously exist in the Mg-Sn-3.0%Y alloy.The particle shape of MgSnY and Sn3Y5 phase,inherited from the solidification,has little change before and after hot extrusion.Mg-Sn-3.0%Y alloy has the highest ultimate tensile strength(UTS),305 MPa,by over 50%compared with that of the other two alloys.
基金Projects (50901017,50731002) supported by the National Natural Science Foundation of ChinaProject (20090042120008) supported by Doctoral Program Foundation of Institutions of Higher Education of ChinaProjects (N100702001,N090502002) supported by the Fundamental Research Funds of the Central Universities,China
文摘The phase equilibria and compositions in Mg-rich comer at 300℃ were determined in the Mg-Zn-A1 ternary system through the equilibrated alloy method by using X-ray diffraction （XRD） and scanning electron microscopy （SEM） assisted with energy dispersive spectroscopy of X-ray （EDS）. The results show that there exist three three-phase regions consisted of a-Mg＋Mg17A112（7）＋A15Mg11Zn4（φ）, a-Mg＋Mga2（Al, Zn）49（r）＋A15MgllZn4（φ） and a-Mg＋MgZn＋Mg32（A1, Zn）49（r）, respectively. The intermetallic compounds in equilibrium with a-Mg phase all have large composition ranges, not appear to be linear. At the same time, both zinc and aluminum are soluble in the a-Mg solid solution, with which the compounds are in equilibrium.