Nd-Fe-B permanent magnets with a small amount of A1 nano-particles doping were prepared by conventional sintered method. Effect of AI content on magnetic property, corrosion resistance and oxidation properties of the ...Nd-Fe-B permanent magnets with a small amount of A1 nano-particles doping were prepared by conventional sintered method. Effect of AI content on magnetic property, corrosion resistance and oxidation properties of the magnets were studied. Inves- tigation showed that the coercivity rose gradually, while the remanence decreased simultaneously with increase of A1 doping amount. Further investigation revealed that most A1 element diffused into the main phase and some A1 element diffused into the Nd-rich phase The autoclave test results showed that the corrosion rate of the magnets decreased with A1 content increasing. After oxidation, the maximum energy product losses of the magnets with 0.0 wt.% and 0.2 wt.% AI nano-particles doping were 6.13% and 3.99%, respec- tively. Therefore, A1 nano-particles doping was a promising way to enhance the coercivity and corrosion resistance of sintered Nd-Fe-B magnet.展开更多
基金Project supported by National Natural Science Foundation of China(51001002)Research Fund for the Doctoral Program of Higher Education of China(20091103120024)+3 种基金National High Technology Research and Development Program of China(2012AA063201)the Key Program of Science and Technology Development Project of Beijing Municipal Education Commission(KZ201110005007)the Importation and Development of High-Caliber Talents Project of Beijing Municipal Institutions211 Project of Beijing University of Technology and Rixin Talents of Beijing Universityof Technology for financial support
文摘Nd-Fe-B permanent magnets with a small amount of A1 nano-particles doping were prepared by conventional sintered method. Effect of AI content on magnetic property, corrosion resistance and oxidation properties of the magnets were studied. Inves- tigation showed that the coercivity rose gradually, while the remanence decreased simultaneously with increase of A1 doping amount. Further investigation revealed that most A1 element diffused into the main phase and some A1 element diffused into the Nd-rich phase The autoclave test results showed that the corrosion rate of the magnets decreased with A1 content increasing. After oxidation, the maximum energy product losses of the magnets with 0.0 wt.% and 0.2 wt.% AI nano-particles doping were 6.13% and 3.99%, respec- tively. Therefore, A1 nano-particles doping was a promising way to enhance the coercivity and corrosion resistance of sintered Nd-Fe-B magnet.
基金Sponsored by State Key Laboratory of Rare Earth Permanent Magnetic Materials(SKLREPM17OF06)National Natural Science Foundation of China(51871201)Key R&D Project of Zhejiang Provincial Department of Science and Technology(2021C01172)。