The corrosion performance of aluminum/steel contact and aluminum/steel FSW joint in 3.5 wt.%NaCl solution were analyzed using potentiostatic tests.The post-corrosion microstructure of the welding joint was characteriz...The corrosion performance of aluminum/steel contact and aluminum/steel FSW joint in 3.5 wt.%NaCl solution were analyzed using potentiostatic tests.The post-corrosion microstructure of the welding joint was characterized by optical microscope(OM),scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).The results showed that the localized corrosion of FSW joint of Al/steel dissimilar metals mainly initiated at the interface transition zone(ITZ).Precipitation of intermetallic compounds(IMCs)and Fe-rich phase particles in ITZ accelerated the corrosion of the FSW joint.This phenomenon has been attributed to distinct corrosion potentials between IMCs and steel,aluminum base metal.The corrosion resistance sequence of IMCs in ITZ is Fe_(3)Al>FeAl>Fe_(2)Al_(5).展开更多
The precipitated phases in the WNZ,TMAZ,HAZ and BM of the friction stir welding(FSW)joint were observed using the transmission electron microscopy(TEM)and the lattice fringe spacing of the precipitated phases was meas...The precipitated phases in the WNZ,TMAZ,HAZ and BM of the friction stir welding(FSW)joint were observed using the transmission electron microscopy(TEM)and the lattice fringe spacing of the precipitated phases was measured.Combined with X-ray diffraction(XRD),the types of precipitated phases among the joint were confirmed and then the strength mismatch mechanism was revealed.The results show the precipitated phases of 7075 aluminum alloy FSW joint mainly consist of MgZn_(2),AlCuMg and Al_(2)CuMg.The microzone of the joint experienced different thermal cycles,the types and sizes of precipitated phases are different and the strengthening effect is different.The strengthening effect of the AlCuMg and Al_(2)CuMg are better than that of MgZn_(2).The precipitated phase in the WNZ mainly includes AlCuMg and Al_(2)CuMg,as well as the grain size is fine,the microhardness in this zone is pretty high.The number of precipitated phase AlCuMg and Al_(2)CuMg is smaller in the TMAZ and the MgZn_(2)is relatively more,which lead the microhardness decrease.The number of precipitated phase MgZn_(2)is relative larger in the HAZ,as well as the grain coarsening,the microhardness in this zone is lowest of the joint.At the same time,there are the precipitate free zones(PFZ)among the 7075 aluminum alloy FSW joint,which decreases the microhardness of the whole joint to some extent.展开更多
In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial micr...In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial microstructure evolution and mechanical properties of Al/Cu dissimilar joints were explored.The experiments were carried out under the rotation rates of 600,900 and 1200 r/min and with the travel speeds of 30,70 and 100 mm/min.The characteristic of interface transition zones(ITZs)and the species of intermetallic compounds(IMCs)were investigated.The Al/Cu interface showed a layered structure composed of Al-Cu IMCs,which will affect the mechanical property.The layer consisting of Al2Cu was formed at lower heat input,and as heat input increased the Al4Cu9 phase started to form.Excessive heat input will increase the thickness of the interface and raise the brittleness of the joints.The thickness of the IMCs layers changed from0.89μm to 3.96μm as the heat input increased.The maximum value of tensile shear loading of 4.65 kN was obtained at the rotation rate of900 r/min and travel speed of 100 mm/min with the interface thickness of 2.89μm.The fracture mode of the joints was a mix of ductile and brittle fracture.展开更多
基金supported by the Natural Science Foundation of Hebei(Grant No.E2019210292)Education Department of Hebei(Grant No.ZD2019102).
文摘The corrosion performance of aluminum/steel contact and aluminum/steel FSW joint in 3.5 wt.%NaCl solution were analyzed using potentiostatic tests.The post-corrosion microstructure of the welding joint was characterized by optical microscope(OM),scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).The results showed that the localized corrosion of FSW joint of Al/steel dissimilar metals mainly initiated at the interface transition zone(ITZ).Precipitation of intermetallic compounds(IMCs)and Fe-rich phase particles in ITZ accelerated the corrosion of the FSW joint.This phenomenon has been attributed to distinct corrosion potentials between IMCs and steel,aluminum base metal.The corrosion resistance sequence of IMCs in ITZ is Fe_(3)Al>FeAl>Fe_(2)Al_(5).
基金supported by the Natural Science Foundation of Hebei(Grant No.E2012210001)Natural Science Foundation of Jiangsu(Grant No.BK20141181)。
文摘The precipitated phases in the WNZ,TMAZ,HAZ and BM of the friction stir welding(FSW)joint were observed using the transmission electron microscopy(TEM)and the lattice fringe spacing of the precipitated phases was measured.Combined with X-ray diffraction(XRD),the types of precipitated phases among the joint were confirmed and then the strength mismatch mechanism was revealed.The results show the precipitated phases of 7075 aluminum alloy FSW joint mainly consist of MgZn_(2),AlCuMg and Al_(2)CuMg.The microzone of the joint experienced different thermal cycles,the types and sizes of precipitated phases are different and the strengthening effect is different.The strengthening effect of the AlCuMg and Al_(2)CuMg are better than that of MgZn_(2).The precipitated phase in the WNZ mainly includes AlCuMg and Al_(2)CuMg,as well as the grain size is fine,the microhardness in this zone is pretty high.The number of precipitated phase AlCuMg and Al_(2)CuMg is smaller in the TMAZ and the MgZn_(2)is relatively more,which lead the microhardness decrease.The number of precipitated phase MgZn_(2)is relative larger in the HAZ,as well as the grain coarsening,the microhardness in this zone is lowest of the joint.At the same time,there are the precipitate free zones(PFZ)among the 7075 aluminum alloy FSW joint,which decreases the microhardness of the whole joint to some extent.
基金supported by the Key project of Education Department of Hebei Province(Grant No.ZD2019102)。
文摘In this study,friction stir lap welding(FSLW)was performed for the welding test of 6061 aluminium alloy and T2 pure copper.The effect of process parameters containing rotation rate and travel speed on interfacial microstructure evolution and mechanical properties of Al/Cu dissimilar joints were explored.The experiments were carried out under the rotation rates of 600,900 and 1200 r/min and with the travel speeds of 30,70 and 100 mm/min.The characteristic of interface transition zones(ITZs)and the species of intermetallic compounds(IMCs)were investigated.The Al/Cu interface showed a layered structure composed of Al-Cu IMCs,which will affect the mechanical property.The layer consisting of Al2Cu was formed at lower heat input,and as heat input increased the Al4Cu9 phase started to form.Excessive heat input will increase the thickness of the interface and raise the brittleness of the joints.The thickness of the IMCs layers changed from0.89μm to 3.96μm as the heat input increased.The maximum value of tensile shear loading of 4.65 kN was obtained at the rotation rate of900 r/min and travel speed of 100 mm/min with the interface thickness of 2.89μm.The fracture mode of the joints was a mix of ductile and brittle fracture.