Bulk anisotropic Sm_(2)Co_(7) nanocrystalline magnets were successfully prepared by hot deformation process using spark plasma sintering technology.The coercivity of the isotropic Sm_(2)Co_(7) nanocrystalline magnet i...Bulk anisotropic Sm_(2)Co_(7) nanocrystalline magnets were successfully prepared by hot deformation process using spark plasma sintering technology.The coercivity of the isotropic Sm_(2)Co_(7) nanocrystalline magnet is 34.76 kOe,further,the ultra-high coercivity of 50.68 kOe is obtained in the anisotropic hot deformed Sm_(2)Co_(7) magnet when the height reduction is70%,which is much higher than those of the ordinarily produced hot deformed Sm_(2)Co_(7) magnet.X-ray diffraction(XRD)analysis shows that all the samples are Sm_(2)Co_(7) single phase.The investigation by electron backscatter diffraction indicates that increasing the amount of deformation is beneficial to the improvement of the(001) texture of Sm_(2)Co_(7) magnets.The Sm_(2)Co_(7) nanocrystalline magnet generates a strong c-axis crystallographic texture during large deformation process.展开更多
基金Project supports by the Science Center of the National Natural Science Foundation of China(Grant No.52088101)the National Natural Foundation of China(Grant No.51590880)+2 种基金the Fujian Institute of Innovation,Chinese Academy of Sciences(Grant No.FJCXY18040302)the Key Program of the Chinese Academy of Sciences(Grant No.KJZD-EW-M05-1)the Natural Science Foundation of Inner Mongolia,China(Grant Nos.2018LH05006 and2018LH05011)。
文摘Bulk anisotropic Sm_(2)Co_(7) nanocrystalline magnets were successfully prepared by hot deformation process using spark plasma sintering technology.The coercivity of the isotropic Sm_(2)Co_(7) nanocrystalline magnet is 34.76 kOe,further,the ultra-high coercivity of 50.68 kOe is obtained in the anisotropic hot deformed Sm_(2)Co_(7) magnet when the height reduction is70%,which is much higher than those of the ordinarily produced hot deformed Sm_(2)Co_(7) magnet.X-ray diffraction(XRD)analysis shows that all the samples are Sm_(2)Co_(7) single phase.The investigation by electron backscatter diffraction indicates that increasing the amount of deformation is beneficial to the improvement of the(001) texture of Sm_(2)Co_(7) magnets.The Sm_(2)Co_(7) nanocrystalline magnet generates a strong c-axis crystallographic texture during large deformation process.