High purity SiC crystal was used as a passive monitor to measure neutron irradiation temperature in the 49-2 research reactor.The SiC monitors were irradiated with fast neutrons at elevated temperatures to 3.2×10...High purity SiC crystal was used as a passive monitor to measure neutron irradiation temperature in the 49-2 research reactor.The SiC monitors were irradiated with fast neutrons at elevated temperatures to 3.2×10^(20)n/cm^(2).The isochronal and isothermal annealing behaviors of the irradiated SiC were investigated by x-ray diffraction and four-point probe techniques.Invisible point defects and defect clusters are found to be the dominating defect types in the neutron-irradiated SiC.The amount of defect recovery in SiC reaches a maximum value after isothermal annealing for 30 min.Based on the annealing temperature dependences of both lattice swelling and material resistivity,the irradiation temperature of the SiC monitors is determined to be~410℃,which is much higher than the thermocouple temperature of 275℃ recorded during neutron irradiation.The possible reasons for the difference are carefully discussed.展开更多
文摘High purity SiC crystal was used as a passive monitor to measure neutron irradiation temperature in the 49-2 research reactor.The SiC monitors were irradiated with fast neutrons at elevated temperatures to 3.2×10^(20)n/cm^(2).The isochronal and isothermal annealing behaviors of the irradiated SiC were investigated by x-ray diffraction and four-point probe techniques.Invisible point defects and defect clusters are found to be the dominating defect types in the neutron-irradiated SiC.The amount of defect recovery in SiC reaches a maximum value after isothermal annealing for 30 min.Based on the annealing temperature dependences of both lattice swelling and material resistivity,the irradiation temperature of the SiC monitors is determined to be~410℃,which is much higher than the thermocouple temperature of 275℃ recorded during neutron irradiation.The possible reasons for the difference are carefully discussed.