The effect of molybdenum oxide on the activity and durability of Ce O2-Ti O2 catalyst for NO reduction by NH3 was examined. It was found that the introduction of Mo could improve the low-temperature NH3-SCR activity a...The effect of molybdenum oxide on the activity and durability of Ce O2-Ti O2 catalyst for NO reduction by NH3 was examined. It was found that the introduction of Mo could improve the low-temperature NH3-SCR activity and SO2/H2 O durability of the Ce O2-Ti O2 catalyst and an optimal loading of Mo was 4?wt.%. The best Mo O3/Ce O2-Ti O2 catalyst displayed over 90% NO conversion from 200 °C to 400 °C and obtained 4-fold increase in NO conversion compared to Ce O2-Ti O2 at 150 °C. The characterization results revealed that the number of Br?nsted acid sites over Mo O3/Ce O2-Ti O2 was significantly increased, and the adsorption of nitrate species was dramatically weakened because of the coverage of Mo O3, which were favorable for the high NH3-SCR performance. It is believed that the Mo O3/Ce O2-Ti O2 catalyst is a suitable substitute for the NH3-SCR reaction.展开更多
Cerium‐based catalysts are very attractive for the catalytic abatement of nitrogen oxides(NOx)emitted from stationary sources.However,the main challenge is still achieving satisfactory catalytic activity in the low‐...Cerium‐based catalysts are very attractive for the catalytic abatement of nitrogen oxides(NOx)emitted from stationary sources.However,the main challenge is still achieving satisfactory catalytic activity in the low‐temperature range and tolerance to SO2 poisoning.In the present work,two series of Mo‐modified CeO_(2)catalysts were respectively obtained through a wet impregnation method(Mo‐CeO_(2))and a co‐precipitation method(MoCe‐cp),and the roles of the Mo species were systematically investigated.Activity tests showed that the Mo‐CeO_(2)catalyst displayed much higher NO conversion at low temperature and anti‐SO2 ability than MoCe‐cp.The optimal Mo‐CeO_(2)catalyst displayed over 80%NO elimination efficiency even at 150°C and remarkable SO2 resistance at 250°C(nearly no activity loss after 40 h test).The characterization results indicated that the introduced Mo species were highly dispersed on the Mo‐CeO_(2)catalyst surface,thereby providing more Brønsted acid sites and inhibiting the formation of stable adsorbed NOx species.These factors synergistically promote the selective catalytic reduction(SCR)reaction in accordance with the Eley‐Rideal(E‐R)reaction path on the Mo‐CeO_(2)catalyst.Additionally,the molybdenum surface could protect CeO_(2)from SO2 poisoning;thus,the reducibility of the Mo‐CeO_(2)catalyst declined slightly to an adequate level after sulfation.The results in this work indicate that surface modification with Mo species may be a simple method of developing highly efficient cerium‐based SCR catalysts with superior SO2 durability.展开更多
基金supported by the National Natural Science Foundation of China(21773106,21707066,21677069,and 21806077)the China Postdoctoral Science Foundation(2018M642206)~~
文摘The effect of molybdenum oxide on the activity and durability of Ce O2-Ti O2 catalyst for NO reduction by NH3 was examined. It was found that the introduction of Mo could improve the low-temperature NH3-SCR activity and SO2/H2 O durability of the Ce O2-Ti O2 catalyst and an optimal loading of Mo was 4?wt.%. The best Mo O3/Ce O2-Ti O2 catalyst displayed over 90% NO conversion from 200 °C to 400 °C and obtained 4-fold increase in NO conversion compared to Ce O2-Ti O2 at 150 °C. The characterization results revealed that the number of Br?nsted acid sites over Mo O3/Ce O2-Ti O2 was significantly increased, and the adsorption of nitrate species was dramatically weakened because of the coverage of Mo O3, which were favorable for the high NH3-SCR performance. It is believed that the Mo O3/Ce O2-Ti O2 catalyst is a suitable substitute for the NH3-SCR reaction.
文摘Cerium‐based catalysts are very attractive for the catalytic abatement of nitrogen oxides(NOx)emitted from stationary sources.However,the main challenge is still achieving satisfactory catalytic activity in the low‐temperature range and tolerance to SO2 poisoning.In the present work,two series of Mo‐modified CeO_(2)catalysts were respectively obtained through a wet impregnation method(Mo‐CeO_(2))and a co‐precipitation method(MoCe‐cp),and the roles of the Mo species were systematically investigated.Activity tests showed that the Mo‐CeO_(2)catalyst displayed much higher NO conversion at low temperature and anti‐SO2 ability than MoCe‐cp.The optimal Mo‐CeO_(2)catalyst displayed over 80%NO elimination efficiency even at 150°C and remarkable SO2 resistance at 250°C(nearly no activity loss after 40 h test).The characterization results indicated that the introduced Mo species were highly dispersed on the Mo‐CeO_(2)catalyst surface,thereby providing more Brønsted acid sites and inhibiting the formation of stable adsorbed NOx species.These factors synergistically promote the selective catalytic reduction(SCR)reaction in accordance with the Eley‐Rideal(E‐R)reaction path on the Mo‐CeO_(2)catalyst.Additionally,the molybdenum surface could protect CeO_(2)from SO2 poisoning;thus,the reducibility of the Mo‐CeO_(2)catalyst declined slightly to an adequate level after sulfation.The results in this work indicate that surface modification with Mo species may be a simple method of developing highly efficient cerium‐based SCR catalysts with superior SO2 durability.