La0.75Mg0.25Ni3.5–xCo0.2Alx （x=0–0.09） hydrogen storage alloys were prepared by induction melting and effect of Al substitution for Ni on phase constitution and electrochemical property was investigated.With the s...La0.75Mg0.25Ni3.5–xCo0.2Alx （x=0–0.09） hydrogen storage alloys were prepared by induction melting and effect of Al substitution for Ni on phase constitution and electrochemical property was investigated.With the substitution of Al for Ni,LaNi5 and LaNi2 phases occurred and （La,Mg）2（Ni,Co,Al）7 phase with hexagonal Ce2Ni7-type structure replaced （La,Mg）2（Ni,Co）7 phase.The cell volumes of LaNi5 and （La,Mg）2（Ni,Co,Al）7 main phases increased with increasing Al content.Some electrochemical properties and kinetic parameters of the alloys,including discharge capacity,high rate discharge ability （HRD）,loss angle （ψ）,exchange current density （I0） and limiting current density （IL）,decreased with increasing amount of substitution of Al for Ni.Substitution of Al for Ni could be favorable for positive shift in corrosion potential of the alloy electrode,and prolonged cyclic lifetime of La0.75Mg0.25Ni3.5–xCo0.2Alx （x=0–0.09） alloy electrodes.展开更多
The microstructural features of hypoeutectic AI-10%Si alloy were observed using optical microscopy and electron backscatter diffraction. The results show that primary silicon particles are frequently found in hypoeute...The microstructural features of hypoeutectic AI-10%Si alloy were observed using optical microscopy and electron backscatter diffraction. The results show that primary silicon particles are frequently found in hypoeutectic alloys. Hence, the nucleation and growth mechanisms of the precipitation of primary silicon of hypoeutectic Al-10%Si alloy melts were investigated. It was discovered that Si atoms are easy to segregate and form Si-Si clusters, which results in the formation of primary silicon even in eutectic or hypoeutectic Al-Si alloys. In addition, solute redistribution caused by chemical driving force and large pile-ups or micro-segregation of the solute play an important role in the formation of the primary silicon, and the solute redistribution equations were derived from Jackson-Chalmers equations. Once Si solute concentration exceeds eutectic composition, primary silicon precipitates are formed at the front of solid/liquid interface.展开更多
基金Project supported by National 863 Program of China (2007AA03Z227, 2007AA03Z230)Natural Science Foundation of Hebei Province (E2010000301)+1 种基金Natural Science Research Planned Project of Hebei University (2009-152)Undergraduate Science and Technology Innovation Project of Hebei University (2010060)
文摘La0.75Mg0.25Ni3.5–xCo0.2Alx （x=0–0.09） hydrogen storage alloys were prepared by induction melting and effect of Al substitution for Ni on phase constitution and electrochemical property was investigated.With the substitution of Al for Ni,LaNi5 and LaNi2 phases occurred and （La,Mg）2（Ni,Co,Al）7 phase with hexagonal Ce2Ni7-type structure replaced （La,Mg）2（Ni,Co）7 phase.The cell volumes of LaNi5 and （La,Mg）2（Ni,Co,Al）7 main phases increased with increasing Al content.Some electrochemical properties and kinetic parameters of the alloys,including discharge capacity,high rate discharge ability （HRD）,loss angle （ψ）,exchange current density （I0） and limiting current density （IL）,decreased with increasing amount of substitution of Al for Ni.Substitution of Al for Ni could be favorable for positive shift in corrosion potential of the alloy electrode,and prolonged cyclic lifetime of La0.75Mg0.25Ni3.5–xCo0.2Alx （x=0–0.09） alloy electrodes.
基金Project (U1134101) supported by the Mutual Foundation of Basic Research of High Speed Railway,ChinaProjects (ZR2009FL003,ZR2010EL011,ZR2011EMM003) supported by the Natural Science Foundation of Shandong Province,China
文摘The microstructural features of hypoeutectic AI-10%Si alloy were observed using optical microscopy and electron backscatter diffraction. The results show that primary silicon particles are frequently found in hypoeutectic alloys. Hence, the nucleation and growth mechanisms of the precipitation of primary silicon of hypoeutectic Al-10%Si alloy melts were investigated. It was discovered that Si atoms are easy to segregate and form Si-Si clusters, which results in the formation of primary silicon even in eutectic or hypoeutectic Al-Si alloys. In addition, solute redistribution caused by chemical driving force and large pile-ups or micro-segregation of the solute play an important role in the formation of the primary silicon, and the solute redistribution equations were derived from Jackson-Chalmers equations. Once Si solute concentration exceeds eutectic composition, primary silicon precipitates are formed at the front of solid/liquid interface.