Nanocrystalline and amorphous LaMg11Ni+x%Ni(x=100,200,mass fraction)alloys were synthesized by mechanicalmilling.The electrochemical hydrogen storage properties of the as-milled alloys were tested by an automatic galv...Nanocrystalline and amorphous LaMg11Ni+x%Ni(x=100,200,mass fraction)alloys were synthesized by mechanicalmilling.The electrochemical hydrogen storage properties of the as-milled alloys were tested by an automatic galvanostatic system.The gaseous hydrogen absorption and desorption properties were investigated by Sievert’s apparatus and differential scanningcalorimeter(DSC)connected with a H2detector.The results indicated that increasing Ni content significantly improves the gaseousand electrochemical hydrogen storage performances of the as-milled alloys.The gaseous hydrogen absorption capacities andabsorption rates of the as-milled alloys have the maximum values with the variation of the milling time.But the hydrogen desorptionkinetics of the alloys always increases with the extending of milling time.In addition,the electrochemical discharge capacity andhigh rate discharge(HRD)ability of the as-milled alloys both increase first and then decrease with milling time prolonging.展开更多
基金Projects(51161015,51371094,51471054) supported by the National Natural Science Foundation of China
文摘Nanocrystalline and amorphous LaMg11Ni+x%Ni(x=100,200,mass fraction)alloys were synthesized by mechanicalmilling.The electrochemical hydrogen storage properties of the as-milled alloys were tested by an automatic galvanostatic system.The gaseous hydrogen absorption and desorption properties were investigated by Sievert’s apparatus and differential scanningcalorimeter(DSC)connected with a H2detector.The results indicated that increasing Ni content significantly improves the gaseousand electrochemical hydrogen storage performances of the as-milled alloys.The gaseous hydrogen absorption capacities andabsorption rates of the as-milled alloys have the maximum values with the variation of the milling time.But the hydrogen desorptionkinetics of the alloys always increases with the extending of milling time.In addition,the electrochemical discharge capacity andhigh rate discharge(HRD)ability of the as-milled alloys both increase first and then decrease with milling time prolonging.