The Bi3＋ doped molybdate-based red-emitting phosphors, LiEu1-xBix（MoO4）2, were successfully synthesized with a sol-gel method. The prepared LiEu1-xBix（MoO4）2 phosphors exhibited pure and intense red emission at 6...The Bi3＋ doped molybdate-based red-emitting phosphors, LiEu1-xBix（MoO4）2, were successfully synthesized with a sol-gel method. The prepared LiEu1-xBix（MoO4）2 phosphors exhibited pure and intense red emission at 613 nm under the excitation of near-UV 394 nm. It was discussed in detail that the influence of the synthesis conditions such as the doping concentration of Bi3, the dose of citric acid, pH of the precursor solution and the sintering temperature on the emission intensity of the phosphors. According to the results, the optimal condition was obtained： the doping concentration of Bi3＋ was 15 mol.%, molar ratio of citric acid to metal ions was 1.5：1, pH of the precursor solution was 1.0 and the sintering temperature was 800 ℃. The X-ray diffraction （XRD） patterns of the LiEuo.85Bi0.15（MoO4）2 phosphor prepared under the optimal condition indicated that the phosphor was single phase with tetragonal scheelite structure. The Commission Intemationale de I＇E- clairage （CIE） chromaticity coordinates of LiEuo.85Bio.15（MoO4）2 were （x=0.655, y=0.345）, which were closer to the national television stan- dard committee （NTSC） standard values （x=0.670, y=0.330） than that of a commercial red phosphor of Y202S：Eu3＋（x=0.630, y=0.350）. This LiEuo.85Bi0As（MoO4）2 red phosphor is a promising candidate for the fabrication of white light-emitting diode （W-LED） with near-UV chips.展开更多
Electrochemical reaction between K4[Fe(CN)6] and K3[Fe(CN)6] on glass electrodedeposited with In2O3 was studide with graze ellipsometry combined with cyclic voltammetry. Theresults indicated that graze ellipsometry po...Electrochemical reaction between K4[Fe(CN)6] and K3[Fe(CN)6] on glass electrodedeposited with In2O3 was studide with graze ellipsometry combined with cyclic voltammetry. Theresults indicated that graze ellipsometry possessed not only time-resolved function, but also space-resolved function. Graze ellipsometrical parameters refiected some information of physicochemicalproperties of interface and diffusion layer near the electrode surface. Change of the pattern of thegraze ellipsometric parameters represented change of rules of the physicochemical properties. Andthe rules revealed the order to random situation of the particles’ distribution near the electrodesurface and were helpful to analyze the properties of the diffusion layer reliably.展开更多
基金Project supported by National Natural Science Foundation of China (NSFC20803097, NSFC20603049)Natural Science Foundation of Chongqing (CSTC2011AB4056, CSTC2009BA4023)the Fundamental Research Funds for the Central Universities (CDJZR10220005 and CDJRC10220002)
文摘The Bi3＋ doped molybdate-based red-emitting phosphors, LiEu1-xBix（MoO4）2, were successfully synthesized with a sol-gel method. The prepared LiEu1-xBix（MoO4）2 phosphors exhibited pure and intense red emission at 613 nm under the excitation of near-UV 394 nm. It was discussed in detail that the influence of the synthesis conditions such as the doping concentration of Bi3, the dose of citric acid, pH of the precursor solution and the sintering temperature on the emission intensity of the phosphors. According to the results, the optimal condition was obtained： the doping concentration of Bi3＋ was 15 mol.%, molar ratio of citric acid to metal ions was 1.5：1, pH of the precursor solution was 1.0 and the sintering temperature was 800 ℃. The X-ray diffraction （XRD） patterns of the LiEuo.85Bi0.15（MoO4）2 phosphor prepared under the optimal condition indicated that the phosphor was single phase with tetragonal scheelite structure. The Commission Intemationale de I＇E- clairage （CIE） chromaticity coordinates of LiEuo.85Bio.15（MoO4）2 were （x=0.655, y=0.345）, which were closer to the national television stan- dard committee （NTSC） standard values （x=0.670, y=0.330） than that of a commercial red phosphor of Y202S：Eu3＋（x=0.630, y=0.350）. This LiEuo.85Bi0As（MoO4）2 red phosphor is a promising candidate for the fabrication of white light-emitting diode （W-LED） with near-UV chips.
文摘Electrochemical reaction between K4[Fe(CN)6] and K3[Fe(CN)6] on glass electrodedeposited with In2O3 was studide with graze ellipsometry combined with cyclic voltammetry. Theresults indicated that graze ellipsometry possessed not only time-resolved function, but also space-resolved function. Graze ellipsometrical parameters refiected some information of physicochemicalproperties of interface and diffusion layer near the electrode surface. Change of the pattern of thegraze ellipsometric parameters represented change of rules of the physicochemical properties. Andthe rules revealed the order to random situation of the particles’ distribution near the electrodesurface and were helpful to analyze the properties of the diffusion layer reliably.