A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical perf...A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical performance of the composite cathode material were investigated by X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and electrochemical tests. The Fe2P content, morphology and electrochemical performance of LiFePOa/（C＋Fe2P） composite depend on the calcination temperature. The optimized LiFePO4/（C＋FeeP） composite is prepared at 650 ~C and the optimized composite exhibits sphere-like morphology with porous structure and Fe2P content of about 3.2% （mass fraction）. The discharge capacity of the optimized LiFePO4/（C＋FeRP） at 0.1C is 156 and 161 mA.h/g at 25 and 55 ℃, respectively, and the corresponding capacity retentions are 96% after 30 cycles; while the capacity at 1C is 142 and 149 mA.h/g at 25 and 55 ℃, respectively, and the capacity still remains 135 and 142 mA-h/g after 30 cycles at 25 and 55℃, respectively.展开更多
基金Project(50571091) supported by the National Natural Science Foundation of ChinaProject(09C947) supported by the Scientific Research Fund of Hunan Provincial Education Department,China
文摘A LiFePO4/（C＋Fe2P） composite cathode material was prepared by a sol-gel method using Fe（NO3）3.9H20, LiAc·H2O）, NHaH2PO4 and citric acid as raw materials, and the physical properties and electrochemical performance of the composite cathode material were investigated by X-ray diffractometry （XRD）, scanning electron microscopy （SEM）, transmission electron microscopy （TEM） and electrochemical tests. The Fe2P content, morphology and electrochemical performance of LiFePOa/（C＋Fe2P） composite depend on the calcination temperature. The optimized LiFePO4/（C＋FeeP） composite is prepared at 650 ~C and the optimized composite exhibits sphere-like morphology with porous structure and Fe2P content of about 3.2% （mass fraction）. The discharge capacity of the optimized LiFePO4/（C＋FeRP） at 0.1C is 156 and 161 mA.h/g at 25 and 55 ℃, respectively, and the corresponding capacity retentions are 96% after 30 cycles; while the capacity at 1C is 142 and 149 mA.h/g at 25 and 55 ℃, respectively, and the capacity still remains 135 and 142 mA-h/g after 30 cycles at 25 and 55℃, respectively.