A new design route was presented to fabricate cobalt aluminum-layered double hydroxide(CoAl-LDH)thin layers whichgrow on carbon spheres(CSs)through a growth method.The CoAl-LDH thin layers consist of nanoflakes with a...A new design route was presented to fabricate cobalt aluminum-layered double hydroxide(CoAl-LDH)thin layers whichgrow on carbon spheres(CSs)through a growth method.The CoAl-LDH thin layers consist of nanoflakes with a thickness of20nm.The galvanostatic charge-discharge test of the CoAl-LDH/CSs composite shows a great specific capacitance of1198F/g at1A/g(based on the mass of the CoAl-LDH/CSs composite)in6mol/L KOH solution,and the composite displays an impressive specificcapacitance of920F/g even at a high current density of10A/g.Moreover,the composite remains a specific capacitance of928F/gafter1000cycles at2A/g,and the specific capacitance retention is84%,indicating that the composite has high specific capacitance,excellent rate capability and good cycling stability in comparison to pristine CoAl-LDH.展开更多
A promising Co3O4/Cu O composite electrode material was successfully synthesized through a facile hydrothermal and calcination process. Effects of the surfactants hexadecyltrimethyl ammonium bromide（CTAB） and polyvi...A promising Co3O4/Cu O composite electrode material was successfully synthesized through a facile hydrothermal and calcination process. Effects of the surfactants hexadecyltrimethyl ammonium bromide（CTAB） and polyvinylpyrrolidone（PVP） on the morphology and electrochemical performance of the composite were investigated. Powder X-ray diffraction（XRD）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM） and nitrogen adsorption-desorption experiment were employed to characterize the microstructures and morphologies of the composite. Meanwhile, the electrochemical performances of the samples were studied using cyclic voltammetry（CV）, galvanostatic charge-discharge test and electrochemical impedance spectroscopy（EIS）. The results show that the porous Co3O4/Cu O-CTAB nanoplates own the best performance and exhibits a high specific capacitance of 398 F/g at 1 A/g with almost 100% capacitance retention over 2000 cycles, and it retains 90% of capacitance at 10 A/g.展开更多
基金Project(21471162) supported by the National Natural Science Foundation of ChinaProject(2015H6016) supported by the Science and Technology Project of Fujian Province,China
文摘A new design route was presented to fabricate cobalt aluminum-layered double hydroxide(CoAl-LDH)thin layers whichgrow on carbon spheres(CSs)through a growth method.The CoAl-LDH thin layers consist of nanoflakes with a thickness of20nm.The galvanostatic charge-discharge test of the CoAl-LDH/CSs composite shows a great specific capacitance of1198F/g at1A/g(based on the mass of the CoAl-LDH/CSs composite)in6mol/L KOH solution,and the composite displays an impressive specificcapacitance of920F/g even at a high current density of10A/g.Moreover,the composite remains a specific capacitance of928F/gafter1000cycles at2A/g,and the specific capacitance retention is84%,indicating that the composite has high specific capacitance,excellent rate capability and good cycling stability in comparison to pristine CoAl-LDH.
基金Project(21471162)supported by the National Natural Science Foundation of ChinaProject(2014LY36)supported by the Science and Technology Project of Longyan CityChina
文摘A promising Co3O4/Cu O composite electrode material was successfully synthesized through a facile hydrothermal and calcination process. Effects of the surfactants hexadecyltrimethyl ammonium bromide（CTAB） and polyvinylpyrrolidone（PVP） on the morphology and electrochemical performance of the composite were investigated. Powder X-ray diffraction（XRD）, scanning electron microscopy（SEM）, transmission electron microscopy（TEM） and nitrogen adsorption-desorption experiment were employed to characterize the microstructures and morphologies of the composite. Meanwhile, the electrochemical performances of the samples were studied using cyclic voltammetry（CV）, galvanostatic charge-discharge test and electrochemical impedance spectroscopy（EIS）. The results show that the porous Co3O4/Cu O-CTAB nanoplates own the best performance and exhibits a high specific capacitance of 398 F/g at 1 A/g with almost 100% capacitance retention over 2000 cycles, and it retains 90% of capacitance at 10 A/g.