Bioleaching experiments combined with X-ray photoelectron spectroscopy(XPS),X-ray diffraction(XRD)and scanning electron microscopy(SEM)were conducted to investigate three kinds of bornites from different regions leach...Bioleaching experiments combined with X-ray photoelectron spectroscopy(XPS),X-ray diffraction(XRD)and scanning electron microscopy(SEM)were conducted to investigate three kinds of bornites from different regions leached by moderately thermophilic mixed bacteria of Leptospirillum ferriphilum YSK,Acidithiobacillus caldus D1 and Sulfobacillus thermosulfidooxidans ST.The results of bioleaching experiments showed that the leaching efficiency and the redox potential were significantly increased.The copper extraction efficiencies of three kinds of bornite maintained rapid growth until around the 12th day and no longer increased after the 18th,reaching 83.7%,96.5%and 86.6%,respectively.The XRD results of the leaching residue indicated that three kinds of bornites all produced jarosite in the late stage of leaching,and the leaching residues from of Daye Museum and Yunnan Geological Museum contained a mass of elemental sulfur.XPS analysis and scanning electron microscopy experiments showed that the surface of mineral particles was jarosite and the copper in the leaching residue was almost dissolved.展开更多
The phase transformation of chalcopyrite and the effect of its phase status on bacterial leaching were studied. Under the protection of high-purity argon, different temperatures(203, 382 and 552℃) were applied to nat...The phase transformation of chalcopyrite and the effect of its phase status on bacterial leaching were studied. Under the protection of high-purity argon, different temperatures(203, 382 and 552℃) were applied to natural chalcopyrite to complete the phase change. In addition, the chalcopyrite was bioleached before and after the phase change. The results show that the chalcopyrite heated at 203 and 382℃ remained in the α phase, whereas the chalcopyrite changed from α to β phase at 552℃. The leaching rates of chalcopyrite after the phase transitions at 203, 382 and 552℃ were 32.9%, 40.5% and 60.95%, respectively. Further, the crystal lattice parameters of chalcopyrite increased and lattice energy decreased, which were the fundamental reasons for the significant increase in leaching rate. Electrochemical experiments demonstrated that with increasing annealing temperature, the polarization resistance decreased and corrosion current density increased. The higher the oxidation rate was, the higher the leaching rate was.展开更多
基金Project(51974363)supported by the National Natural Science Foundation of China。
文摘Bioleaching experiments combined with X-ray photoelectron spectroscopy(XPS),X-ray diffraction(XRD)and scanning electron microscopy(SEM)were conducted to investigate three kinds of bornites from different regions leached by moderately thermophilic mixed bacteria of Leptospirillum ferriphilum YSK,Acidithiobacillus caldus D1 and Sulfobacillus thermosulfidooxidans ST.The results of bioleaching experiments showed that the leaching efficiency and the redox potential were significantly increased.The copper extraction efficiencies of three kinds of bornite maintained rapid growth until around the 12th day and no longer increased after the 18th,reaching 83.7%,96.5%and 86.6%,respectively.The XRD results of the leaching residue indicated that three kinds of bornites all produced jarosite in the late stage of leaching,and the leaching residues from of Daye Museum and Yunnan Geological Museum contained a mass of elemental sulfur.XPS analysis and scanning electron microscopy experiments showed that the surface of mineral particles was jarosite and the copper in the leaching residue was almost dissolved.
基金Project(2018zzts768) supported by the Fundamental Research Funds for the Central South University,ChinaProject(51204207) supported by the National Natural Science Foundation of China
文摘The phase transformation of chalcopyrite and the effect of its phase status on bacterial leaching were studied. Under the protection of high-purity argon, different temperatures(203, 382 and 552℃) were applied to natural chalcopyrite to complete the phase change. In addition, the chalcopyrite was bioleached before and after the phase change. The results show that the chalcopyrite heated at 203 and 382℃ remained in the α phase, whereas the chalcopyrite changed from α to β phase at 552℃. The leaching rates of chalcopyrite after the phase transitions at 203, 382 and 552℃ were 32.9%, 40.5% and 60.95%, respectively. Further, the crystal lattice parameters of chalcopyrite increased and lattice energy decreased, which were the fundamental reasons for the significant increase in leaching rate. Electrochemical experiments demonstrated that with increasing annealing temperature, the polarization resistance decreased and corrosion current density increased. The higher the oxidation rate was, the higher the leaching rate was.