The 12 mm-thick Ti−6Al−4V(TC4)titanium alloy plates were welded using keyhole tungsten inert gas(K-TIG)welding at various heat inputs.The microstructure,grain boundary(GB)characteristics and mechanical properties of t...The 12 mm-thick Ti−6Al−4V(TC4)titanium alloy plates were welded using keyhole tungsten inert gas(K-TIG)welding at various heat inputs.The microstructure,grain boundary(GB)characteristics and mechanical properties of the weld metal zone(WMZ)were analyzed.The test results show that the K-TIG welds are well formed,and no obvious defects are observed when the heat input is 2.30−2.62 kJ/mm.When the heat input gradually increases,αlaths increase in length,andα′phase and residualβphase are reduced.The electron backscatter diffraction(EBSD)test results indicate that the high-angle GB proportion in the WMZ increases with the increase of heat input.The tensile strength of the WMZ gradually decreases and the elongation of the WMZ increases when the heat input increases from 2.30 to 2.62 kJ/mm.The impact toughness of the WMZ increases as the heat input increases.展开更多
基金The authors are grateful for the financial supports from the Key Research and Development Program of Guangdong Province,China(2020B090928003)the Natural Science Foundation of Guangdong Province,China(2020A1515011050)+1 种基金the Science and Technology Base and Talent Special Project of Guangxi Province,China(AD19245150)Guangxi University of Science and Technology Doctoral Fund,China(19Z27).
文摘The 12 mm-thick Ti−6Al−4V(TC4)titanium alloy plates were welded using keyhole tungsten inert gas(K-TIG)welding at various heat inputs.The microstructure,grain boundary(GB)characteristics and mechanical properties of the weld metal zone(WMZ)were analyzed.The test results show that the K-TIG welds are well formed,and no obvious defects are observed when the heat input is 2.30−2.62 kJ/mm.When the heat input gradually increases,αlaths increase in length,andα′phase and residualβphase are reduced.The electron backscatter diffraction(EBSD)test results indicate that the high-angle GB proportion in the WMZ increases with the increase of heat input.The tensile strength of the WMZ gradually decreases and the elongation of the WMZ increases when the heat input increases from 2.30 to 2.62 kJ/mm.The impact toughness of the WMZ increases as the heat input increases.