The NiCoCrAlY coatings strengthened by three nano-particles with the same addition were prepared on a Ni-base super alloy using laser cladding technique. The dry frictional wear behaviors of the coatings at 500 ℃ in ...The NiCoCrAlY coatings strengthened by three nano-particles with the same addition were prepared on a Ni-base super alloy using laser cladding technique. The dry frictional wear behaviors of the coatings at 500 ℃ in static air were investigated. The comparison was made with the coating without nano-particles. The results show that the wear mechanism of the NiCoCrAlY coatings with nano-particles, like the coating without nano-particles, is the delamination wear due to the strong plastic deformation and oxidative wear. However, the frictional coefficient of the coatings increases and presents the decrease trend with the increase of sliding distance after adding nano-particles. Moreover, the wear rate of the coatings with nano-particles is only 34.0%-64.5% of the coating without nano-particles. Among the three nano-particles, the improvement of nano-SiC on the high temperature wear resistance of the coating is the most significant.展开更多
The nanometer Al2O3 dispersion strengthened NiCoCrAlY high-temperature protective coatings by crosscurrent CO2 laser on Ni-based superalloy GH4033 were produced. Microscopic morphologies, phase constitutions of claddi...The nanometer Al2O3 dispersion strengthened NiCoCrAlY high-temperature protective coatings by crosscurrent CO2 laser on Ni-based superalloy GH4033 were produced. Microscopic morphologies, phase constitutions of cladding coatings and distribution of nano-Al2O3 particles were examined using SEM and XRD. The results show that the interface grains, after adding proper nano-Al2O3, grow from epitaxial to non-epitaxial shape gradually, and the columnar dendrites become thinner and denser with cellular shape. Cracks in the substrate close to the interface are eliminated. Moreover, dispersive nano-Al2O3 particles mainly distribute around cellular substructure and on grain-boundaries, which prevents the diffusion of alloying elements and restrains the formation of new phase. There is a critical value of nano-Al2O3 addition, and the most suitable content of nano-Al2O3 is 1% (mass fraction) in this experimental conditions. The "nanometer effect" of nano-Al2O3 particles plays an important role in the improvement of coating microstructure.展开更多
基金Project(20060287019)supported by the Research Fund for Doctoral Program of Higher Education of ChinaProject(kjsmcx07001)supported by the Opening Research Fund of Jiangsu Key Laboratory of Tribology,ChinaProject(BK2010267)supported by the Jiangsu Provincial Natural Science Foundation of Jiangsu Province,China
文摘The NiCoCrAlY coatings strengthened by three nano-particles with the same addition were prepared on a Ni-base super alloy using laser cladding technique. The dry frictional wear behaviors of the coatings at 500 ℃ in static air were investigated. The comparison was made with the coating without nano-particles. The results show that the wear mechanism of the NiCoCrAlY coatings with nano-particles, like the coating without nano-particles, is the delamination wear due to the strong plastic deformation and oxidative wear. However, the frictional coefficient of the coatings increases and presents the decrease trend with the increase of sliding distance after adding nano-particles. Moreover, the wear rate of the coatings with nano-particles is only 34.0%-64.5% of the coating without nano-particles. Among the three nano-particles, the improvement of nano-SiC on the high temperature wear resistance of the coating is the most significant.
基金Project(20060287019) supported by the Research Fund for Doctoral Program of Higher Education of ChinaProject(kjsmcx07001) supported by the Opening Research Fund of Jiangsu Key Laboratory of Tribology, ChinaProject(CX08B-039Z) supported by the Graduate Innovation Foundation of Jiangsu Province, China
文摘The nanometer Al2O3 dispersion strengthened NiCoCrAlY high-temperature protective coatings by crosscurrent CO2 laser on Ni-based superalloy GH4033 were produced. Microscopic morphologies, phase constitutions of cladding coatings and distribution of nano-Al2O3 particles were examined using SEM and XRD. The results show that the interface grains, after adding proper nano-Al2O3, grow from epitaxial to non-epitaxial shape gradually, and the columnar dendrites become thinner and denser with cellular shape. Cracks in the substrate close to the interface are eliminated. Moreover, dispersive nano-Al2O3 particles mainly distribute around cellular substructure and on grain-boundaries, which prevents the diffusion of alloying elements and restrains the formation of new phase. There is a critical value of nano-Al2O3 addition, and the most suitable content of nano-Al2O3 is 1% (mass fraction) in this experimental conditions. The "nanometer effect" of nano-Al2O3 particles plays an important role in the improvement of coating microstructure.