To develop an improved approach in achieving an excellent combination of high strength and ductility,the solutionized Al?Cu?Li plates were subjected to rolling at cryogenic and room temperatures,respectively,to a redu...To develop an improved approach in achieving an excellent combination of high strength and ductility,the solutionized Al?Cu?Li plates were subjected to rolling at cryogenic and room temperatures,respectively,to a reduction of83%,followed by aging treatment at160°C.The results indicate that Al?Cu?Li alloys through cryogenic rolling followed by aging treatment possess better mechanical properties.Rolling at cryogenic temperature produces a high density of dislocations because of the suppression of dynamic recovery,which in turn promotes the precipitation of T1(Al2CuLi)precipitates during aging.Such high density of T1precipitates enable effective dislocation pinning,leading to an increase in strength and ductility.In contrast,room temperature rolled alloys after aging treatment exhibit lower strength and ductility due to low density of T1precipitates in the grain interior and high density of T1precipitates around subgrain boundaries.展开更多
The effect of pre-recovery on the recrystallization kinetics of a supersaturated Al–Mn alloy annealed at 530°C was investigated.The results show that the pre-recovery treatment can lead to faster recrystallizati...The effect of pre-recovery on the recrystallization kinetics of a supersaturated Al–Mn alloy annealed at 530°C was investigated.The results show that the pre-recovery treatment can lead to faster recrystallization kinetics at the initial stage but cause sluggish recrystallization at the later stage.This different recrystallization behavior is explained by the formation of precipitates-free zones and the consumption of driving force during the pre-recovery treatment.The promoted recrystallization at the early stage can be interpreted by the promotion of recrystallization nucleation through sub-grain growth to a critical size inside precipitates-free zones.A simple model is presented to describe the nucleation of recrystallization with pre-recovery treatment in the supersaturated Al–Mn alloys.展开更多
基金Projects (106112015CDJXZ138803,106112015CDJXY130003) supported by the Fundamental Research Funds for the Central Universities,ChinaProject (51421001) supported by National Natural Science Foundation of China
文摘To develop an improved approach in achieving an excellent combination of high strength and ductility,the solutionized Al?Cu?Li plates were subjected to rolling at cryogenic and room temperatures,respectively,to a reduction of83%,followed by aging treatment at160°C.The results indicate that Al?Cu?Li alloys through cryogenic rolling followed by aging treatment possess better mechanical properties.Rolling at cryogenic temperature produces a high density of dislocations because of the suppression of dynamic recovery,which in turn promotes the precipitation of T1(Al2CuLi)precipitates during aging.Such high density of T1precipitates enable effective dislocation pinning,leading to an increase in strength and ductility.In contrast,room temperature rolled alloys after aging treatment exhibit lower strength and ductility due to low density of T1precipitates in the grain interior and high density of T1precipitates around subgrain boundaries.
基金Project(2016YFB0300901)supported by National Key R&D Program of ChinaProject(51421001)supported by the National Natural Science Foundation of ChinaProject(106112015CDJXY130003)supported by the Fundamental Research Funds for the Central Universities,China
文摘The effect of pre-recovery on the recrystallization kinetics of a supersaturated Al–Mn alloy annealed at 530°C was investigated.The results show that the pre-recovery treatment can lead to faster recrystallization kinetics at the initial stage but cause sluggish recrystallization at the later stage.This different recrystallization behavior is explained by the formation of precipitates-free zones and the consumption of driving force during the pre-recovery treatment.The promoted recrystallization at the early stage can be interpreted by the promotion of recrystallization nucleation through sub-grain growth to a critical size inside precipitates-free zones.A simple model is presented to describe the nucleation of recrystallization with pre-recovery treatment in the supersaturated Al–Mn alloys.