The setting reaction of glass ionomer cement was studied by analyzing and comparing the short-tem mechanical properties of set cement stored in silicone oil, air and distilled water respectively at different temperatu...The setting reaction of glass ionomer cement was studied by analyzing and comparing the short-tem mechanical properties of set cement stored in silicone oil, air and distilled water respectively at different temperatures. For the set cement stored at 37 ℃, the strength of the sample in the air reached the maximum value after 24 h, then decreased to about 210 MPa and kept steady. The strength of the sample in water increased continuously and slowly, however, the increasing rate of sample stored in silicone oil was higher than that in the water. At 20 ℃, the increasing rate of compressive strength for sample in air was higher than those in silicone oil and water. The diffusion speed and maintenance of water has significant effects on the mechanical properties of glass ionomer cements.展开更多
We examined P53 mutation and invasion front grading (IFG) in 30 cases of oral squamous cell carcinomas (OSCCs). The association of P53 mutation and IFG scores with clinicopa-thological parameters was evaluated. P53 mu...We examined P53 mutation and invasion front grading (IFG) in 30 cases of oral squamous cell carcinomas (OSCCs). The association of P53 mutation and IFG scores with clinicopa-thological parameters was evaluated. P53 mutation existed in exon 5-8 in 15 out of the 30 OSCCs (50%). The incidence of P53 mutation was not associated with age, gender, N value and TNM stage. However, there was a significant correlation between P53 mutation and T value (P=0.046). There were no statistically significant correlations among the clinicopathological parameters and IFG. Interestingly, The IFG score in OSCCs with P53 mutation was significantly higher than that in OSCCs without P53 mutation (P<0.001). These results suggest that the high incidence of P53 mutation is a major mechanism of OSCC carcinogenesis. The presence of P53 mutation indicates the most anaplastic fields in the invasive areas of the tumors, which may predict poor prognosis for the patients.展开更多
文摘The setting reaction of glass ionomer cement was studied by analyzing and comparing the short-tem mechanical properties of set cement stored in silicone oil, air and distilled water respectively at different temperatures. For the set cement stored at 37 ℃, the strength of the sample in the air reached the maximum value after 24 h, then decreased to about 210 MPa and kept steady. The strength of the sample in water increased continuously and slowly, however, the increasing rate of sample stored in silicone oil was higher than that in the water. At 20 ℃, the increasing rate of compressive strength for sample in air was higher than those in silicone oil and water. The diffusion speed and maintenance of water has significant effects on the mechanical properties of glass ionomer cements.
文摘We examined P53 mutation and invasion front grading (IFG) in 30 cases of oral squamous cell carcinomas (OSCCs). The association of P53 mutation and IFG scores with clinicopa-thological parameters was evaluated. P53 mutation existed in exon 5-8 in 15 out of the 30 OSCCs (50%). The incidence of P53 mutation was not associated with age, gender, N value and TNM stage. However, there was a significant correlation between P53 mutation and T value (P=0.046). There were no statistically significant correlations among the clinicopathological parameters and IFG. Interestingly, The IFG score in OSCCs with P53 mutation was significantly higher than that in OSCCs without P53 mutation (P<0.001). These results suggest that the high incidence of P53 mutation is a major mechanism of OSCC carcinogenesis. The presence of P53 mutation indicates the most anaplastic fields in the invasive areas of the tumors, which may predict poor prognosis for the patients.