AlN/GaN resonant tunneling diodes(RTDs)were grown separately on freestanding Ga N(FS-GaN)substrates and sapphire substrates by plasma-assisted molecular-beam epitaxy(PA-MBE).Room temperature negative differential resi...AlN/GaN resonant tunneling diodes(RTDs)were grown separately on freestanding Ga N(FS-GaN)substrates and sapphire substrates by plasma-assisted molecular-beam epitaxy(PA-MBE).Room temperature negative differential resistance(NDR)was obtained under forward bias for the RTDs grown on FS-GaN substrates,with the peak current densities(Jp)of 175-700 kA/cm^(2)and peak-to-valley current ratios(PVCRs)of 1.01-1.21.Two resonant peaks were also observed for some RTDs at room temperature.The effects of two types of substrates on epitaxy quality and device performance of GaN-based RTDs were firstly investigated systematically,showing that lower dislocation densities,flatter surface morphology,and steeper heterogeneous interfaces were the key factors to achieving NDR for RTDs.展开更多
基金Project supported by the National Key R&D Program of China(Grant No.2018YFB0406600)the National Natural Science Foundation of China(Grant Nos.61875224,61804163,and 61827823)+2 种基金Key Laboratory of Microelectronic Devices and Integration Technology,Chinese Academy of Sciences(Grant No.Y9TAQ21)Key Laboratory of Nano-devices and Applications,Chinese Academy of Sciences(Grant No.Y8AAQ21001)Guangxi Key Laboratory of Precision Navigation Technology and Application,Guilin University of Electronic Technology(Grant No.DH202011)。
文摘AlN/GaN resonant tunneling diodes(RTDs)were grown separately on freestanding Ga N(FS-GaN)substrates and sapphire substrates by plasma-assisted molecular-beam epitaxy(PA-MBE).Room temperature negative differential resistance(NDR)was obtained under forward bias for the RTDs grown on FS-GaN substrates,with the peak current densities(Jp)of 175-700 kA/cm^(2)and peak-to-valley current ratios(PVCRs)of 1.01-1.21.Two resonant peaks were also observed for some RTDs at room temperature.The effects of two types of substrates on epitaxy quality and device performance of GaN-based RTDs were firstly investigated systematically,showing that lower dislocation densities,flatter surface morphology,and steeper heterogeneous interfaces were the key factors to achieving NDR for RTDs.