A new technique for preparing semisolid slurry,namely,distributary-confluence runner(DCR),was combined with die-casting(DC)to conduct rheological die-casting(R-DC)of A356 alloy.The mechanism of DCR for semisolid slurr...A new technique for preparing semisolid slurry,namely,distributary-confluence runner(DCR),was combined with die-casting(DC)to conduct rheological die-casting(R-DC)of A356 alloy.The mechanism of DCR for semisolid slurry preparation was determined via numerical simulations and experiments.The microstructure and mechanical properties of A356 alloys prepared via DC and R-DC were studied.High-quality slurry containing numerous primary α-Al(α1-Al)with an average size of 49μm and a shape factor of 0.81 could be prepared via DCR.Simulation results indicated that the unique flow state and physical field changes during slurry preparation were conducive to accelerating the uniformity of melt temperature and composition fields,nucleation exfoliation,and spherical growth.Compared with the alloy prepared via DC,the tensile strength,yield strength,and elongation of A356 alloy prepared via R-DC increased by 19%,15%,and 107%,respectively.展开更多
基金the financial supports from the National Natural Science Foundation of China(Nos.52005034,52027805)the Beijing Postdoctoral Research Foundation(No.2021-ZZ-073)+2 种基金the China Postdoctoral Science Foundation Funded Project(2021M691860)the Fundamental Research Funds for the Central Universities(No.FRF-TP-18-043A1)the Zhuhai Industry-University-Research Cooperation Project(No.ZH22017001200176PWC).
文摘A new technique for preparing semisolid slurry,namely,distributary-confluence runner(DCR),was combined with die-casting(DC)to conduct rheological die-casting(R-DC)of A356 alloy.The mechanism of DCR for semisolid slurry preparation was determined via numerical simulations and experiments.The microstructure and mechanical properties of A356 alloys prepared via DC and R-DC were studied.High-quality slurry containing numerous primary α-Al(α1-Al)with an average size of 49μm and a shape factor of 0.81 could be prepared via DCR.Simulation results indicated that the unique flow state and physical field changes during slurry preparation were conducive to accelerating the uniformity of melt temperature and composition fields,nucleation exfoliation,and spherical growth.Compared with the alloy prepared via DC,the tensile strength,yield strength,and elongation of A356 alloy prepared via R-DC increased by 19%,15%,and 107%,respectively.