Pre-cold rolling with low reductions(<3%)was used to improve the mechanical properties of rolled ZK60 plates.The effects of rolling path on mechanical properties were investigated in detail.Both pre-cold rolling al...Pre-cold rolling with low reductions(<3%)was used to improve the mechanical properties of rolled ZK60 plates.The effects of rolling path on mechanical properties were investigated in detail.Both pre-cold rolling along the transverse direction(TD)and pre-cold rolling along the normal direction(ND)can increase the yield strength.However,pre-cold rolling along the TD is more effective than pre-cold rolling along the ND in improving the comprehensive mechanical properties.After pre-cold rolling to 3%reduction,the sample rolled along the TD and the sample rolled along the ND have similar tensile yield strength(~270 MPa).However,the former has a higher compressive yield strength,lower yield asymmetry and larger toughness than the latter.Moreover,pre-cold rolling can also enhance precipitation hardening effect.However,aging treatment cannot further improve the yield strength of pre-cold rolled samples.Finally,the related mechanism is discussed.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51601154)the Fundamental Research Funds for the Central Universities, China (No. XDJK2019B003)+1 种基金the Natural Science Foundation of Jiangsu Higher Education Institutions of China (No. 17KJD430006)Chongqing Municipal Education Commission, China (No. KJZDK202001502)
文摘Pre-cold rolling with low reductions(<3%)was used to improve the mechanical properties of rolled ZK60 plates.The effects of rolling path on mechanical properties were investigated in detail.Both pre-cold rolling along the transverse direction(TD)and pre-cold rolling along the normal direction(ND)can increase the yield strength.However,pre-cold rolling along the TD is more effective than pre-cold rolling along the ND in improving the comprehensive mechanical properties.After pre-cold rolling to 3%reduction,the sample rolled along the TD and the sample rolled along the ND have similar tensile yield strength(~270 MPa).However,the former has a higher compressive yield strength,lower yield asymmetry and larger toughness than the latter.Moreover,pre-cold rolling can also enhance precipitation hardening effect.However,aging treatment cannot further improve the yield strength of pre-cold rolled samples.Finally,the related mechanism is discussed.