Conventional,submicron and multimodal WC-12Co cermet coatings were deposited by high velocity oxy-fuel（HVOF）.The microhardness and microstructure of the coatings were compared,and the resistance of the coatings to c...Conventional,submicron and multimodal WC-12Co cermet coatings were deposited by high velocity oxy-fuel（HVOF）.The microhardness and microstructure of the coatings were compared,and the resistance of the coatings to cavitation erosion was studied by ultrasonic vibration cavitation equipment.Cavitation pits and craters were observed by SEM and cavitation mechanisms were explored.The results show that the microstructures of submicron and multimodal WC-12Co coatings prepared by HVOF are dense with little porosity,and their microhardness values are obviously higher than that of the conventional WC-12Co coating.The average microhardness of multimodal WC-12Co coating reaches nearly HV1500,which is much higher than that of the conventional one.As well,it is found that the multimodal WC-12Co coating exhibits the best cavitation erosion resistance among the three coatings,the erosion rate is approximately 40% that of the conventional coating,and the cavitation erosion resistance of multimodal WC-12Co coating is enhanced by above 150% in comparison with the conventional coating.展开更多
A comprehensive study of the phase composition, microstructure evolution, microhardness and wear performance of WC-12 Co composite coatings fabricated by laser cladding using coaxial powder-feed mode was presented. It...A comprehensive study of the phase composition, microstructure evolution, microhardness and wear performance of WC-12 Co composite coatings fabricated by laser cladding using coaxial powder-feed mode was presented. It was shown that a combination of high scan speed and high laser energy density made WC on the edge of WC-12 Co composite powders partially melt in liquid Co and 304 stainless steel matrix, and then new carbides consisting of lamellar WC and herringbone M3 W3 C(M=Fe,Co) were formed. Meanwhile, WC-12 Co composite coatings with no porosity, cracks and drawbacks like decarburization were obtained, showing high densification and good metallurgical bonding with the substrate. Furthermore, a considerably high microhardness of HV0.3 1500-1600, low coefficient of friction of 0.55 and wear rate of(2.15±0.31)×10-7 mm3/(N·m) were achieved owing to the synergistic effect of excellent metallurgical bonding and fine microstructures of composite coating under laser power of 1500 W.展开更多
基金Project(50479016) supported by the National Natural Science Foundation of China
文摘Conventional,submicron and multimodal WC-12Co cermet coatings were deposited by high velocity oxy-fuel（HVOF）.The microhardness and microstructure of the coatings were compared,and the resistance of the coatings to cavitation erosion was studied by ultrasonic vibration cavitation equipment.Cavitation pits and craters were observed by SEM and cavitation mechanisms were explored.The results show that the microstructures of submicron and multimodal WC-12Co coatings prepared by HVOF are dense with little porosity,and their microhardness values are obviously higher than that of the conventional WC-12Co coating.The average microhardness of multimodal WC-12Co coating reaches nearly HV1500,which is much higher than that of the conventional one.As well,it is found that the multimodal WC-12Co coating exhibits the best cavitation erosion resistance among the three coatings,the erosion rate is approximately 40% that of the conventional coating,and the cavitation erosion resistance of multimodal WC-12Co coating is enhanced by above 150% in comparison with the conventional coating.
基金Project(20171ACE50018)supported by the Key Research and Development Program of Jiangxi Province,ChinaProject(2017-YZD2-16)supported by the Key Research Project of Jiangxi Academy of Sciences,China。
文摘A comprehensive study of the phase composition, microstructure evolution, microhardness and wear performance of WC-12 Co composite coatings fabricated by laser cladding using coaxial powder-feed mode was presented. It was shown that a combination of high scan speed and high laser energy density made WC on the edge of WC-12 Co composite powders partially melt in liquid Co and 304 stainless steel matrix, and then new carbides consisting of lamellar WC and herringbone M3 W3 C(M=Fe,Co) were formed. Meanwhile, WC-12 Co composite coatings with no porosity, cracks and drawbacks like decarburization were obtained, showing high densification and good metallurgical bonding with the substrate. Furthermore, a considerably high microhardness of HV0.3 1500-1600, low coefficient of friction of 0.55 and wear rate of(2.15±0.31)×10-7 mm3/(N·m) were achieved owing to the synergistic effect of excellent metallurgical bonding and fine microstructures of composite coating under laser power of 1500 W.