摘要
用固相反应法制备了Pt/C催化剂(Pt/C(s)),并研究了该催化剂对乙醇氧化的电催化活性。XRD和TEM测量表明,Pt/C(s)中Pt的平均粒径为3.8nm,结晶度为2.38,远小于用传统的液相还原方法制得的Pt/C催化剂(Pt/C(1))的平均粒径(8.5nm)和结晶度(5.56)。因此,Pt/C(s)对乙醇的电催化氧化性能远好于液相还原法制得的Pt/C(1)。
The Pt/C catalyst (Pt/C(s)) was prepared with solid phase reaction method and its electrocatalytic activity for the ethanol oxidation was studied. XRD and TEM measurements indicated that the average diameter and the crystalline extent of Pt particles in Pt/C(s) are 3.8 nm and 2.38, respectively, which are much lower than the average diameter(8.5 nm) and the crystalline extent(5.56) of the Pt/C(l) catalyst prepared with the traditional liquid phase reaction method(Pt/C(l)). Therefore, the electrocatalytic activity of Pt/C(s) for the ethanol oxidation is much better than that of Pt/C(l). Cyclic voltammograms and chronoamperometric curves both confirmed this conclusion.
出处
《物理化学学报》
SCIE
CAS
CSCD
北大核心
2003年第11期1001-1004,共4页
Acta Physico-Chimica Sinica
基金
国家基础研究重大项目计划(G2000026408)
国家高技术研究计划(2001AA323060)
国家自然科学基金(20003005)
江苏省自然科学基金BQ2000009)
江苏省教育厅高新技术产业化基金(JH02-080)
吉林省自然科学基金(20000510)
国家"211"工程重点学科建设资助项目~~