PBAT的扩链反应及其微孔发泡行为研究 被引量:13

Study on Chain Extension and Microcellular Foaming Behaviors of Poly(butyleneadipate-co-terephthlate)
下载PDF
导出
摘要 以己二酸丁二醇酯-对苯二甲酸丁二醇酯(PBAT)共聚物为基体,加入不同含量的扩链剂,经熔融共混后,制备扩链PBAT。结果表明,随着扩链剂含量的增加,熔融混合的扭矩值、凝胶含量和结晶温度逐渐升高,熔融温度基本不变,结晶度下降,黏弹性得到改善;以超临界CO_2为物理发泡剂,通过间歇式釜压发泡法制备微孔PBAT泡沫,随着扩链剂含量的增多,发泡样品的泡孔尺寸变小,泡孔密度逐渐增加,当扩链剂的份数为0.8时,泡孔尺寸为4.4μm,泡孔密度为1.65×10~10个/cm^3。 The chain-extended poly(butyleneadipate-co-terephthlate)(PBAT)was prepared by use of different amounts of chain extender through reactive melt blending.An investigation indicated that the torque,gel fraction and crystallization temperature of chain-extended PBAT were improved with an increase of weight fraction of chain extender.However,its melting temperature kept stable,followed by a modification of viscosity,whereas its degree of crystallinity decreased.The micro-foaming PBAT materials were prepared by using supercritical CO 2 as a physical foaming agent.The structural characterizations and performance evaluation indicated that the cell size of PBAT foams decreased with an increase in weight fraction of chain extender,but their cell density was improved.When the weight fraction of chain extender was set as 0.8,the PBAT foams achieved a cell size of 4.4μm and a cell density of 1.65×10 10 cells/cm 3.
作者 宋敬思 王贤增 周洪福 王向东 张玉霞 SONG Jingsi;WANG Xianzeng;ZHOU Hongfu;WANG Xiangdong;ZHANG Yuxia(School of Materials and Mechanical Engineering,Beijing Technology and Business University,Beijing 100048,China;Beijing Key Laboratory of Quality Evaluation Technology for Hygiene and Safety of Plastics,Beijing 100048,China)
出处 《中国塑料》 CAS CSCD 北大核心 2018年第11期42-48,共7页 China Plastics
基金 国家自然科学基金(51703004和51673004) 北京市自然科学基金(2162012) 北京市属高校青年拔尖人才培育计划(CIT&TCD201704041) 科技创新服务能力建设-基本科研业服务费-食品包装用聚合物发泡材料研究平台(PXM2018-014213-000033)
关键词 己二酸丁二醇酯对苯二甲酸丁二醇酯 超临界二氧化碳 扩链 熔体弹性 微孔 poly(butyleneadipate-co-terephthlate) supercritical carbon dioxide chain extension melting elasticity microcellular
  • 相关文献

参考文献7

二级参考文献66

  • 1陈民杰,田国华,张勇,万超瑛,张隐西.二氧化硅对等规聚丙烯和共聚聚丙烯结晶和熔融行为的影响[J].中国塑料,2005,19(10):30-34. 被引量:6
  • 2李云政,李真.淀粉降解树脂中淀粉改性的研究[J].塑料,1996,25(5):18-22. 被引量:3
  • 3R John, D Hans, J Lehermeier. Polylactides: Properties and Prospects of an Environmentally Benign Plastic from Renewable Resources [J]. Macromolecular Symposia, 2001, 175(1): 55-66. 被引量:1
  • 4Y Byun, Y T Kim, S Whiteside. Characterization of an Antioxidant Polylactie Acid(PLA) Film Prepared with a- tocopherol, BHT and Polyethylene Glycol Using Film Cast Extrude[J].Journal of Food Engineering, 2010, 100(2) : 239-244. 被引量:1
  • 5R E Drumright, P R gruber, D E Henton. Polylactic Acid Technology[J]. Journal Advanced Materials , 2000, 12 (23) : 1841-1846. 被引量:1
  • 6W T Zhai, Y Ko, W Zhu, et al. A Study of the Crystalli- zation, Melting, and Foaming Behaviors of Polylactic Acid in Compressed CO2 [J]. International Journal of Molecular Science, 2009, 10: 5381-5397. 被引量:1
  • 7D Garlotta. A Literature Review of Poly(lactic acid)[J]. Journal of Polymers & Environment, 2001, 9(2) : 63-84. 被引量:1
  • 8A G Mikos, A J Thorsen, L A Czerwonka. Preparation and Characterization of Poly(L-lactic acid) Foams [J].Polymer,1994, 35(5) : 1068-1077. 被引量:1
  • 9H B Li, M A Huneault. Effect of Chain Extension on the Properties of PLA/TPS Blends [J]. Journal of Applied Polymer Science , 2011, 122(1) : 134-141. 被引量:1
  • 10S S Ray, M Okamoto. New Polylactide/Layered SilicateNanocomposites[J]. Macromolecular Materials ~ Engi- neering ,2003, 288: 936-944. 被引量:1

共引文献34

同被引文献97

引证文献13

二级引证文献34

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部