摘要
目的研究316L和2205在淡化海水中的耐腐蚀性能,并研究水处理药剂对不锈钢耐蚀性的影响。方法采用电化学试验、慢应变速率拉伸试验、扫描电镜等方法。结果在淡化海水中,316L临界点蚀温度为42.7℃,加入药剂后为70.2℃;2205的临界点蚀温度大于85℃。2205耐缝隙腐蚀性能明显好于316L,药剂对2205也具有一定的缓蚀作用。316L和2205在50℃淡化海水中具有高应力腐蚀抗力。结论 316L不适合直接在淡化海水中应用,但适合在加入药剂的淡化海水中使用;2205适合在淡化海水中应用。
Objective To study the corrosion resistance of 316L and 2205 stainless steel in desalinated seawater and explore influences of water treatment agentia on corrosion resistance of stainless steel. Methods Electrochemical test, slow strain rate tensile test, SEM, etc. were adopted. Results The critical pitting temperature of 316L in desalinated sea- water was 42.7 ℃. It was 70.2 ℃ after agentia was added; the critical pitting temperature of 2205 was higher than 85 ℃. The crevice corrosion resistance property of 2205 was better than 316L. The agentia also had corrosion inhibition effect on 2205. Both 316L and 2205 had high stress corrosion resistance in desalinated seawater at 50℃. Conclusion 316L is not suitable to be used in desalinated seawater directly, but is suitable to be used in desalinated seawater with agentia; 2205 is suitable to be used in desalinated seawater.
作者
李超
吴恒
张波
盖德胜
LI Chao WU Heng ZHANG Bo GAI De-sheng(Qingdao NCS Testing ＆ Corrosion Protection Technology Co., Ltd., Qingdao 266071, China Qingdao Research Institute four Marine Corrosion, Central Institute for Iron and Steel, Qingdao 266071, China)
出处
《装备环境工程》
CAS
2017年第2期67-71,共5页
Equipment Environmental Engineering
关键词
淡化海水
不锈钢
点蚀
缝隙腐蚀
应力腐蚀
desalinated seawater
stainless steel
pitting
crevice corrosion
stress corrosion